Thermal Evaporation Recipes
Jump to navigation
Jump to search
The printable version is no longer supported and may have rendering errors. Please update your browser bookmarks and please use the default browser print function instead.
Back to Vacuum Deposition Recipes.
Thermal Evaporator 1
Materials Table
Materials Table for Thermal Evaporator #1
| |||||||
---|---|---|---|---|---|---|---|
Material | Symbol | Density, g/cm3 | Z Ratio | Tooling, % | Current, Amp | Dep.rate, A/sec | Comments |
Aluminum | Al | 2.70 | 8.17 | 95 | 85 | 1 | Used often |
Chromium | Cr | 7.20 | 28.95 | 95 | 85 | 2 | Used often |
Cobalt | Co | 8.71 | 25.74 | ||||
Copper | Cu | 8.93 | 20.21 | 100 | Used often | ||
Gold | Au | 19.32 | 23.18 | 101.2 | 122 | 5 | Used often |
Gold/Palladium | Au.5/Pd.5 | 15.86 | 23.96 | ||||
Gold/Palladium | Au.5/Pd.4 | 16.40 | 23.80 | ||||
Gold/Zinc | Au.95/Zn.05 | 18.72 | 22.89 | 101.2 | |||
Gold/Zinc | Au.90/Zn.10 | 18.07 | 22.58 | ||||
Magnezium | Mg | 1.74 | 5.48 | 98.4 | |||
Manganese | Mn | 7.20 | 23.40 | 120 | 100 | ||
Nickel | Ni | 8.90 | 26.68 | 100 | 50 | 4.5 | Used often |
Nichrome | NiCr | 8.32 | 27.59 | 100 | 0.4 | ||
Palladium | Pd | 12.40 | 24.73 | 140.5 | 62 | 1.5 | Used often |
Silicon Monoxide | SiO | 2.13 | 10.19 | 120 | 70 | ||
Silver | Ag | 10.5 | 16.69 | ||||
Zinc | Zn | 7.14 | 17.18 | 50 | 4.5 | Used often | |
Zinc Oxide | ZnO | 5.61 | 15.88 | ||||
Strontium Fluoride | SrF2 | 4.28 | 12.15 | 200 | |||
Iron | Fe | 7.86 | 25.30 | ||||
ITO(IndiumTinOxide) | In2O3 - SnO2 | 6.43-7.14 | 0.841 | ||||
Permalloy | Ni0.1Fe0.2 | 8.7 | 26.40 | 140 | 0.1 |
Thermal Evaporator 2
Materials Table
Materials Table for Thermal Evaporator #2
| |||||
---|---|---|---|---|---|
Material | Symbol | Density, g/cm3 | Z Ratio | Tooling, % | Comments |
Aluminum | Al | 2.70 | 1.08 | ||
Antimony | Sb | 6.620 | 0.768 | ||
Arsenic | As | 5.73 | 0.996 | ||
Beryllium | Be | 1.85 | 0.543 | ||
Boron | B | 2.54 | 0.389 | ||
Cadmium | Cd | 8.64 | 0.682 | ||
Cadmium sulfide | CdS | 4.83 | 1.02 | ||
Cadmium telluride | CdTe | 5.85 | 0.980 | ||
Calcium fluoride | CaF2 | 3.18 | 0.775 | Used often | |
Carbon (graphite) | C | 2.25 | 3.26 | ||
Chromium | Cr | 7.20 | 0.305 | 155 | Used often |
Cobalt | Co | 8.71 | 0.343 | ||
Copper | Cu | 8.93 | 0.437 | ||
Gallium | Ga | 5.93 | 0.593 | ||
Gallium Arsenide | GaAs | 5.31 | 1.59 | ||
Germanium | Ge | 5.35 | 0.516 | ||
Gold | Au | 19.30 | 0.381 | Used often | |
Indium | In | 7.30 | 0.841 | 120 | Used often |
Indium antimonide | InSb | 5.76 | 0.769 | ||
Iridium | Ir | 22.4 | 0.129 | ||
Iron | Fe | 7.86 | 0.349 | ||
Lead | Pb | 11.3 | 1.13 | ||
Lead sulfide | PbS | 7.50 | 0.566 | ||
Lithium fluoride | LiF | 2.638 | 0.778 | ||
Magnesium | Mg | 1.74 | 1.61 | ||
Magnesium oxide | MgO | 3.58 | 0.411 | ||
Magnesium Fluoride | MgF2 | 3.00 ( should be 3.18) | 0.427( should be 0.637) | ||
Manganese | Mn | 7.20 | 0.377 | ||
Manganese(II) Sulfide | MnS | 3.99 | 0.94 | ||
Mercury | Hg | 13.46 | 0.74 | ||
Molybdenum | Mo | 10.2 | 0.257 | ||
Nickel | Ni | 8.91 | 0.331 | Used often | |
Niobium | Nb | 8.578 | 0.492 | ||
Niobium(V) Oxide | Nb2O5 | 4.47 | *1.00 | *z ratio has not been established | |
Palladium | Pd | 12.0 | 0.357 | ||
Platinum | Pt | 21.4 | 0.245 | ||
Potasium Cloride | KCl | 1.98 | 2.05 | ||
Selenium | Se | 4.82 | 0.864 | ||
Silicon | Si | 2.32 | 0.712 | ||
Silicon(II) Oxide | SiO | 2.13 | 0.87 | ||
Silicon dioxide (fused quarz) | SiO2 | 2.20 | 1.07 | ||
Silver | Ag | 10.5 | 0.529 | ||
Silver bromide | AgBr | 6.47 | 1.18 | ||
Silver chloride | AgCl | 5.56 | 1.32 | ||
Sodium | Na | 0.97 | 4.8 | ||
Sodium chloride | NaCl | 2.17 | 1.57 | ||
Tantalum | Ta | 16.6 | 0.262 | ||
Tantalum(IV) oxide | Ta2O5 | 8.2 | 0.30 | ||
Tin | Sn | 7.30 | 0.724 | Used often | |
Titanium | Ti | 4.50 | 0.628 | Used often | |
Titanium (IV) Oxide | TiO2 | 4.26 | 0.40 | ||
Titanium Oxide | TiO | 4.90 | *1.00 | * z ratio not established | |
Tungsten | W | 19.3 | 0.163 | ||
Tungsten carbide | WC | 15.6 | 0.151 | ||
Zinc | Zn | 7.04 | 0.514 | Used often | |
Zinc Oxide | ZnO | 5.61 | 0.556 | ||
Zinc Sulfide | ZnS | 4.09 | 0.775 | ||
Zirconium | Zr | 6.51 | 0.60 | Should be 6.49 | |
Zirconium Oxide | ZrO2 | 5.6 | 1.001 |