[http://www.google.com/url?sa=t&rct=j&q=&esrc=s&source=web&cd=1&cad=rja&ved=0CC4QFjAA&url=http%3A%2F%2Fwww.nanofab.ubc.ca%2Ffiles%2Fclawson2001_iii-v_etching.pdf&ei=pIp6UobsOOTjiAKIw4G4Cw&usg=AFQjCNHo1MN8BZJmexnKIwpn92Rax6N5Lg&sig2=RK4rXPfIeJgcQEH5HkqWWw&bvm=bv.56146854,d.cGE Guide to references on III±V semiconductor chemical etching] Please add any confirmed etches from this reference to the Master Table of Wet Etching. Thanks,
   
 
=Metal Etching=
 
=Metal Etching=

Revision as of 10:31, 6 November 2013


Example Wet Etching Table (Include All Materials)

How to use the wet etch table:

When entering a new etch into the table make a row for every etchant used in the solution such that the information can be sorted by etchant. For example, the InP etch HCl:H3PO4(1:3) and H3PO4:HCl(3:1). Likewise, if etch is known to be selective to multiple materials the etch should have a row for each material. For example HCl:H3PO4(1:3) is selective to both InGaAs and InGaAsP.

This multiple entry method may seem laborious for the person entering a new etch, however the power of sorting by selective materials and chemicals in a table with all materials is great.

Material Etchant Rate (nm/min) Anisotropy Selective to Selectivity Ref. Notes Confirmed by Extra column
InP HCl:H3PO4(1:3) ~1000 Highly InGaAs High [Lamponi (p.102)] Example Jon Doe Example
InP HCl:H3PO4(1:3) ~1000 Highly InGaAsP High [Lamponi (p.102)] Example Jon Doe Example
InP H3PO4:HCl(3:1) ~1000 Highly InGaAs High [Lamponi (p.102)] Example Jon Doe Example
InP H3PO4:HCl(3:1) ~1000 Highly InGaAsP High [Lamponi (p.102)] Example Jon Doe Example


The Master Table of Wet Etching (Include All Materials)

Material Etchant Rate (nm/min) Anisotropy Selective to Selectivity Ref. Notes Confirmed by Extra column
InP HCl:H3PO4(1:3) ~1000 Highly InGaAs High [Lamponi (p.102)] Example Jon Doe Example
InP HCl:H3PO4(1:3) ~1000 Highly InGaAsP High [Lamponi (p.102)] Example Jon Doe Example
InP H3PO4:HCl(3:1) ~1000 Highly InGaAs High [Lamponi (p.102)] Example Jon Doe Example
InP H3PO4:HCl(3:1) ~1000 Highly InGaAsP High [Lamponi (p.102)] Example Jon Doe Example

Compound Semiconductor Etching

Guide to references on III±V semiconductor chemical etching Please add any confirmed etches from this reference to the Master Table of Wet Etching. Thanks,

Metal Etching

Silicon etching

Dielectric etching

Organic removal

Gold Plating

Chemi-Mechanical Polishing (CMP)