! Material !! Etchant !! Rate (nm/min) !! Anisotropy !! Selective to !! Selectivity !! Ref. !! Notes !! Confirmed by !! Extra column
 
! Material !! Etchant !! Rate (nm/min) !! Anisotropy !! Selective to !! Selectivity !! Ref. !! Notes !! Confirmed by !! Extra column
 
|-
 
|-
| InP|| HCl:H3PO4(1:3)|| ~1000 || Highly || InGaAs || High || [[http://tel.archives-ouvertes.fr/docs/00/76/94/02/PDF/VA2_LAMPONI_MARCO_15032012.pdf | Lamponi (p.102)]] || Example || Jon Doe || Example
+
| InP|| HCl:H3PO4(1:3)|| ~1000 || Highly || InGaAs || High || [[http://tel.archives-ouvertes.fr/docs/00/76/94/02/PDF/VA2_LAMPONI_MARCO_15032012.pdf Lamponi (p.102)]] || Example || Jon Doe || Example
 
|-
 
|-
 
| InP|| HCl:H3PO4(1:3)|| ~1000 || Highly || InGaAsP || High || [[http://tel.archives-ouvertes.fr/docs/00/76/94/02/PDF/VA2_LAMPONI_MARCO_15032012.pdf Lamponi (p.102)]] || Example || Jon Doe || Example
 
| InP|| HCl:H3PO4(1:3)|| ~1000 || Highly || InGaAsP || High || [[http://tel.archives-ouvertes.fr/docs/00/76/94/02/PDF/VA2_LAMPONI_MARCO_15032012.pdf Lamponi (p.102)]] || Example || Jon Doe || Example

Revision as of 10:26, 6 November 2013

How to use the wet etch table:

When entering a new etch into the table make a row for every etchant used in the solution such that the information can be sorted by etchant. For example, the InP etch HCl:H3PO4(1:3) and H3PO4:HCl(3:1). Likewise, if etch is known to be selective to multiple materials the etch should have a row for each material. For example HCl:H3PO4(1:3) is selective to both InGaAs and InGaAsP.

This multiple entry method may seem laborious for the person entering a new etch, however the power of sorting by selective materials and chemicals in a table with all materials is great.

Example Wet Etching Table (Include All Materials)

Material Etchant Rate (nm/min) Anisotropy Selective to Selectivity Ref. Notes Confirmed by Extra column
InP HCl:H3PO4(1:3) ~1000 Highly InGaAs High [Lamponi (p.102)] Example Jon Doe Example
InP HCl:H3PO4(1:3) ~1000 Highly InGaAsP High [Lamponi (p.102)] Example Jon Doe Example
InP H3PO4:HCl(3:1) ~1000 Highly InGaAs High [Lamponi (p.102)] Example Jon Doe Example
InP H3PO4:HCl(3:1) ~1000 Highly InGaAsP High [Lamponi (p.102)] Example Jon Doe Example