Difference between revisions of "Wet Etching Recipes"
Jump to navigation
Jump to search
Bovington j (talk | contribs) |
Bovington j (talk | contribs) |
||
| Line 36: | Line 36: | ||
| InP|| H3PO4:HCl(3:1)|| ~1000 || Highly || InGaAsP || High || [[http://tel.archives-ouvertes.fr/docs/00/76/94/02/PDF/VA2_LAMPONI_MARCO_15032012.pdf Lamponi (p.102)]] || Example || Jon Doe || Example |
| InP|| H3PO4:HCl(3:1)|| ~1000 || Highly || InGaAsP || High || [[http://tel.archives-ouvertes.fr/docs/00/76/94/02/PDF/VA2_LAMPONI_MARCO_15032012.pdf Lamponi (p.102)]] || Example || Jon Doe || Example |
||
|- |
|- |
||
| − | | Al2O3 (ALD Plasma 300C)|| 300MIF || ~1.6 || || Most non-Al Materials || High || |
+ | | Al2O3 (ALD Plasma 300C)|| 300MIF || ~1.6 || || Most non-Al Materials || High || Measured in-house || Rate slows with time || JTB || Example |
|- |
|- |
||
| − | | Al2O3 (ALD Plasma 300C)|| |
+ | | Al2O3 (ALD Plasma 300C)|| 400K || ~2.2 || || Most non-Al Materials || High || Measured in-house || Rate slows with time || JTB || Example |
|- |
|- |
||
| − | | Al2O3 (ALD Plasma 300C)|| |
+ | | Al2O3 (ALD Plasma 300C)|| 400K(1:4) || ~1.6 || || Most non-Al Materials || High || Measured in-house || Rate slows with time || JTB || Example |
|- |
|- |
||
| − | | Al2O3 (ALD Plasma 300C)|| |
+ | | Al2O3 (ALD Plasma 300C)|| NH4OH:H2O2:H2O (1:2:50) || ~<0.5 || || || High || Measured in-house || Rate slows with time || JTB || Example |
| + | |- |
||
| + | | Al2O3 (ALD Plasma 300C)|| H2O2:NH4OH:H2O (2:1:50) || ~<0.5 || || || High || Measured in-house || Rate slows with time || JTB || Example |
||
|} |
|} |
||
Revision as of 11:40, 6 November 2013
Example Wet Etching Table
How to use the Master Table of Wet Etching:
When entering a new etch into the table make a row for every etchant used in the solution such that the information can be sorted by etchant. For example, the InP etch HCl:H3PO4(1:3) and H3PO4:HCl(3:1). Likewise, if etch is known to be selective to multiple materials the etch should have a row for each material. For example HCl:H3PO4(1:3) is selective to both InGaAs and InGaAsP.
This multiple entry method may seem laborious for the person entering a new etch, however the power of sorting by selective materials and chemicals in a table with all materials is great.
| Material | Etchant | Rate (nm/min) | Anisotropy | Selective to | Selectivity | Ref. | Notes | Confirmed by | Extra column |
|---|---|---|---|---|---|---|---|---|---|
| InP | HCl:H3PO4(1:3) | ~1000 | Highly | InGaAs | High | [Lamponi (p.102)] | Example | Jon Doe | Example |
| InP | HCl:H3PO4(1:3) | ~1000 | Highly | InGaAsP | High | [Lamponi (p.102)] | Example | Jon Doe | Example |
| InP | H3PO4:HCl(3:1) | ~1000 | Highly | InGaAs | High | [Lamponi (p.102)] | Example | Jon Doe | Example |
| InP | H3PO4:HCl(3:1) | ~1000 | Highly | InGaAsP | High | [Lamponi (p.102)] | Example | Jon Doe | Example |
The Master Table of Wet Etching (Include All Materials)
| Material | Etchant | Rate (nm/min) | Anisotropy | Selective to | Selectivity | Ref. | Notes | Confirmed by | Extra column |
|---|---|---|---|---|---|---|---|---|---|
| InP | HCl:H3PO4(1:3) | ~1000 | Highly | InGaAs | High | [Lamponi (p.102)] | Example | Jon Doe | Example |
| InP | HCl:H3PO4(1:3) | ~1000 | Highly | InGaAsP | High | [Lamponi (p.102)] | Example | Jon Doe | Example |
| InP | H3PO4:HCl(3:1) | ~1000 | Highly | InGaAs | High | [Lamponi (p.102)] | Example | Jon Doe | Example |
| InP | H3PO4:HCl(3:1) | ~1000 | Highly | InGaAsP | High | [Lamponi (p.102)] | Example | Jon Doe | Example |
| Al2O3 (ALD Plasma 300C) | 300MIF | ~1.6 | Most non-Al Materials | High | Measured in-house | Rate slows with time | JTB | Example | |
| Al2O3 (ALD Plasma 300C) | 400K | ~2.2 | Most non-Al Materials | High | Measured in-house | Rate slows with time | JTB | Example | |
| Al2O3 (ALD Plasma 300C) | 400K(1:4) | ~1.6 | Most non-Al Materials | High | Measured in-house | Rate slows with time | JTB | Example | |
| Al2O3 (ALD Plasma 300C) | NH4OH:H2O2:H2O (1:2:50) | ~<0.5 | High | Measured in-house | Rate slows with time | JTB | Example | ||
| Al2O3 (ALD Plasma 300C) | H2O2:NH4OH:H2O (2:1:50) | ~<0.5 | High | Measured in-house | Rate slows with time | JTB | Example |
Compound Semiconductor Etching
Guide to references on III±V semiconductor chemical etching Please add any confirmed etches from this reference to the Master Table of Wet Etching. Thanks,