Test Data of etching SiO2 with CHF3/CF4-ICP1

From UCSB Nanofab Wiki
Jump to navigation Jump to search
The printable version is no longer supported and may have rendering errors. Please update your browser bookmarks and please use the default browser print function instead.
ICP#1 Recipe: 0.5Pa, 50/900W, CHF3/CF4=10/30 sccm, time=210 sec
Date Sample# Etch Rate (nm/min) Etch Selectivity (SiO2/PR) Comments SEM Images
01/11/2023 ND_Pan1_011123 120 1.28 [30D][CS]
12/14/2022 ND_Pan1_121422 118.6 1.30 [30D][CS]
12/09/2022 ND_Pan1_120922 100.6 1.01 double AuPd coat maybe blur image [30D][CS]
11/18/2022 ND_Pan1_111822 132.6 1.25 [30D][CS]
11/07/2022 ND_Pan1_110722 125.7 1.35 [30D] [CS]
10/21/2022 ND_Pan1_102122 114.3 1.15 [30D] [CS]
10/10/2022 ND_Pan1_101022 127.4 1.25 [30D] [CS]
10/3/2022 ND_Pan1_100322 132.9 1.19 High etch rate and selectivity.

May be due to angled ridge.

[30D] [CS]
9/26/2022 ND_Pan1n_092622 111.1 0.90 This is the new wafer [30D] [CS]
9/26/2022 ND_Pan1o_092622 114.3 1.01 This is the old wafer [45D] [CS]
9/12/2022 ND_Pan1_091222 128.6 1.33 New Si wafer, higher etch rate/

selectivity

[30D] [CS]
9/01/2022 ND_Pan1_090122 120.9 1.05 [30D] [CS]
8/22/2022 ND_Pan1_082222 112.9 1.08 Etch Rate seems low

and selectivity on the lower side

[45D] [CS]
8/5/2022 ND_Pan 1_080522 115.1 0.90 [30D] [CS]
7/27/2022 ND_Pan1_072722 134.6 1.12 [CS] [30D]
5/10/2022 NP_ICP1_07 136 1.34 [1] [2]
4/26/2022 NP_ICP1_06 139.4 1.36 [1] [2]
4/20/2022 NP_ICP1_05 140 1.13 [1] [2]
4/13/2022 NP_ICP1_04 140.3 1.24 [1] [2]
3/29/2022 NP_ICP1_03 136.9 1.19 [1][2]
3/8/2022 NP_ICP1_02 133.7 1.12 [1] [2]
3/2/2022 NP_ICP1_01 141.4 1.20 [1] [2]
1/7/2021 I12101 118 1.12 [1]
3/3/2020 I12004 110 1.05 [2]
Sidewall profile on 2/28/2020 etches is slanted, chamber will be wet-cleaned on 3/2/2020 and re-tested. Data for 3/3 shows etch returned to "normal".
2/28/2020 I12003 119 1.17 56.6 [3]
1/23/2020 I12002 109 1.16 [4]
Rate on 1/13/2020 is low by ~20%, so chamber was wet-cleaned on 1/21/2020. Data below for 1/23 shows rate returned to "normal".
1/13/2020 I12001 78.0 1.06 unusual - two regions [5]
5/29/2019 I11903 105 1.41 [6]
1/28/2019 I11901 110 1.35 see SEM → [7]


OLD Etch Test Data

Alternate SiO2 etch recipe with O2 included.

ICP#1: 0.5Pa, 50/500W, CHF3/CF4/O2=35/5/10sccm, time=210 sec
Date Sample# Etch Rate (nm/min) Etch Selectivity (SiO2/PR) Averaged Sidewall Angle (o) SEM Images
1/28/2019 I11902 78.1 0.63 [8]
5/29/2019 I11904 71.1 0.58 [9]
Retrieved from "https://wiki.nanofab.ucsb.edu/w/index.php?title=Test_Data_of_etching_SiO2_with_CHF3/CF4-ICP1&oldid=160838"