Difference between revisions of "Test Data of etching SiO2 with CHF3/CF4-ICP1"

From UCSB Nanofab Wiki
Jump to navigation Jump to search
m (added entry in ICP1 cals)
m (added entry to ICP1 cals)
Line 9: Line 9:
 
|'''Averaged Sidewall Angle (<sup>o</sup>)'''
  
|'''Averaged Sidewall Angle (<sup>o</sup>)'''
 
|'''SEM Images'''
  
|'''SEM Images'''
  +
|-
  +
|4/20/2022
  +
|NP_ICP1_05
  +
|140
  +
|
  +
|
  +
|[https://wiki.nanotech.ucsb.edu/w/images/7/74/ICP1_05_45D_001.jpg <nowiki>[1]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/7/72/ICP1_05_CS_002.jpg <nowiki>[2]</nowiki>]
 
|-
  
|-
 
|4/13/2022
  
|4/13/2022

Revision as of 10:58, 21 April 2022

ICP#1 Recipe: 0.5Pa, 50/900W, CHF3/CF4=10/30 sccm, time=210 sec
Date Sample# Etch Rate (nm/min) Etch Selectivity (SiO2/PR) Averaged Sidewall Angle (o) SEM Images
4/20/2022 NP_ICP1_05 140 [1] [2]
4/13/2022 NP_ICP1_04 140.3 [1] [2]
3/29/2022 NP_ICP1_03 136.9 1.19 [1][2]
3/8/2022 NP_ICP1_02 133.7 1.12 [1] [2]
3/2/2022 NP_ICP1_01 141.4 1.20 [1] [2]
1/7/2021 I12101 118 1.12 [1]
3/3/2020 I12004 110 1.05 [2]
Sidewall profile on 2/28/2020 etches is slanted, chamber will be wet-cleaned on 3/2/2020 and re-tested. Data for 3/3 shows etch returned to "normal".
2/28/2020 I12003 119 1.17 56.6 [3]
1/23/2020 I12002 109 1.16 [4]
Rate on 1/13/2020 is low by ~20%, so chamber was wet-cleaned on 1/21/2020. Data below for 1/23 shows rate returned to "normal".
1/13/2020 I12001 78.0 1.06 unusual - two regions [5]
5/29/2019 I11903 105 1.41 [6]
1/28/2019 I11901 110 1.35 see SEM → [7]


OLD Etch Test Data

Alternate SiO2 etch recipe with O2 included.

ICP#1: 0.5Pa, 50/500W, CHF3/CF4/O2=35/5/10sccm, time=210 sec
Date Sample# Etch Rate (nm/min) Etch Selectivity (SiO2/PR) Averaged Sidewall Angle (o) SEM Images
1/28/2019 I11902 78.1 0.63 [8]
5/29/2019 I11904 71.1 0.58 [9]