Difference between revisions of "Test Data of etching SiO2 with CHF3/CF4-ICP1"

From UCSB Nanofab Wiki
Jump to navigation Jump to search
(new section :pasted data from CHF3/CF4/O2 etch data)
m (added entry to ICP1 historical data)
Line 62: Line 62:
 
|
  
|
 
|[https://wiki.nanotech.ucsb.edu/w/images/4/49/I1210113.pdf]
  
|[https://wiki.nanotech.ucsb.edu/w/images/4/49/I1210113.pdf]
  +
|-
  +
|3/2/2022
  +
|BP_ICP1_01
  +
|141.4
  +
|
  +
|
  +
|[https://wiki.nanotech.ucsb.edu/w/images/4/44/ICP1_01_45D_001.jpg <nowiki>[1]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/8/87/ICP1_01_CS_003.jpg <nowiki>[2]</nowiki>]
 
|}
  
|}
   

Revision as of 12:05, 8 March 2022

ICP#1 Recipe: 0.5Pa, 50/900W, CHF3/CF4=10/30 sccm, time=210 sec
Date Sample# Etch Rate (nm/min) Etch Selectivity (SiO2/PR) Averaged Sidewall Angle (o) SEM Images
1/28/2019 I11901 110 1.35 see SEM → [1]
5/29/2019 I11903 105 1.41 [2]
1/13/2020 I12001 78.0 1.06 unusual - two regions [3]
Rate on 1/13/2020 is low by ~20%, so chamber was wet-cleaned on 1/21/2020. Data below for 1/23 shows rate returned to "normal".
1/23/2020 I12002 109 1.16 [4]
2/28/2020 I12003 119 1.17 56.6 [5]
Sidewall profile on 2/28/2020 etches is slanted, chamber will be wet-cleaned on 3/2/2020 and re-tested. Data below shows etch returned to "normal".
3/3/2020 I12004 110 1.05 [6]
1/7/2021 I12101 118 1.12 [7]
3/2/2022 BP_ICP1_01 141.4 [1] [2]


OLD Etch Test Data

Alternate SiO2 etch recipe with O2 included.

ICP#1: 0.5Pa, 50/500W, CHF3/CF4/O2=35/5/10sccm, time=210 sec
Date Sample# Etch Rate (nm/min) Etch Selectivity (SiO2/PR) Averaged Sidewall Angle (o) SEM Images
1/28/2019 I11902 78.1 0.63 [8]
5/29/2019 I11904 71.1 0.58 [9]
Retrieved from "https://wiki.nanofab.ucsb.edu/w/index.php?title=Test_Data_of_etching_SiO2_with_CHF3/CF4-ICP1&oldid=159704"