Difference between revisions of "Test Data of Etching SiO2 with CHF3/CF4-Fluorine ICP Etcher"

From UCSB Nanofab Wiki
Jump to navigation Jump to search
(pasted Ning's 2nd data table, hilighted recipe changes and comment about data being "in progress")
 
(30 intermediate revisions by 3 users not shown)
Line 1: Line 1:
−
'''''This page is under construction - we are in the process of standardizing and collecting process control data for this tool. -- Demis 2022-02-11'''''
  
   
 
{| class="wikitable"
  
{| class="wikitable"
−
| colspan="6" |Fluorine ICP: 3.8mT, 50/800W, CHF3/CF4=10/30sccm, time=90 sec
 +
| colspan="7" |Fluorine ICP: 3.8mT, 50/'''900W''', CHF3/CF4=10/30sccm, time='''90 sec'''
 
|-
  
|-
 
|Date
  
|Date
−
|Sample#
 +
|Sample #
−
|Etch Rate (nm/min)
 +
|Etch Rate (nm/min)
−
|Etch Selectivity (SiO2/PR)
 +
|Etch Selectivity (SiO2/PR)
−
|Averaged Sidewall Angle (<sup>o</sup>)
 +
|Averaged Sidewalls Angle
  +
|Observations/Notes
−
|SEM Images
  
  +
|SEM Images (45d, cross section)
 
|-
  
|-
−
|1/28/2021
 +
|01/09/23
  +
|ND_FL_010923
−
|FE2102
  
  +
|263.3
−
|309
  
−
|0.99
 +
|1.31
 
|
  
|
  +
|
−
|[https://wiki.nanotech.ucsb.edu/w/images/0/0b/FE210206.pdf]
  
  +
|[https://wiki.nanotech.ucsb.edu/w/images/9/9b/30D_FICP_010923_002.jpg <nowiki>[30D]</nowiki>][https://wiki.nanotech.ucsb.edu/w/images/2/2b/CS_FICP_010923_003.jpg <nowiki>[CS]</nowiki>]
−
|}
  
  +
|-
  +
|12/14/22
  +
|ND_FL_121422
  +
|266.7
  +
|1.29
  +
|
  +
|
  +
|[https://wiki.nanotech.ucsb.edu/w/images/6/62/30D_FICP_121422_002.jpg <nowiki>[30D]</nowiki>][https://wiki.nanotech.ucsb.edu/w/images/5/5b/CS_FICP_121422_002.jpg <nowiki>[CS]</nowiki>]
  +
|-
  +
|12/09/22
  +
|ND_FL_120922
  +
|260
  +
|1.26
  +
|
  +
|
  +
|[https://wiki.nanotech.ucsb.edu/w/images/7/72/30D_FICP_120922_002.jpg <nowiki>[30D]</nowiki>][https://wiki.nanotech.ucsb.edu/w/images/4/4e/CS_FICP_120922_002.jpg <nowiki>[CS]</nowiki>]
  +
|-
  +
|11/18/22
  +
|ND_FL_111822
  +
|268
  +
|1.01
  +
|
  +
|
  +
|[https://wiki.nanotech.ucsb.edu/w/images/6/64/30D_FICP_111822_002.jpg <nowiki>[30D]</nowiki>][https://wiki.nanotech.ucsb.edu/w/images/c/c5/CS_FICP_111822_002.jpg <nowiki>[CS]</nowiki>]
  +
|-
  +
|11/07/22
  +
|ND_FL_110722
  +
|264.7
  +
|0.96
  +
|
  +
|
  +
|[https://wiki.nanotech.ucsb.edu/w/images/c/c8/30D_FICP_110722_002.jpg <nowiki>[30D]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/e/e9/CS_FICP_110722_002.jpg <nowiki>[CS]</nowiki>]
  +
|-
  +
|10/24/22
  +
|ND_FL_102422
  +
|266.7
  +
|1.22
  +
|
  +
|
  +
|[https://wiki.nanotech.ucsb.edu/w/images/3/38/30D_FICP_102422_002.jpg <nowiki>[30D]</nowiki>][https://wiki.nanotech.ucsb.edu/w/images/7/74/CS_FICP_102422_002.jpg <nowiki>[CS]</nowiki>]
  +
|-
  +
|10/14/22
  +
|ND_FL_101422
  +
|249
  +
|0.82
  +
|
  +
|Image drifted very slightly
  +
in SEM. May account for
   
  +
low selectivity.
−  
  +
|[https://wiki.nanotech.ucsb.edu/w/images/7/76/30D_FICP_101422_002.jpg <nowiki>[30D]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/c/ca/CS_FICP_101422_003.jpg <nowiki>[CS]</nowiki>]
−
{| class="wikitable"
  
−
| colspan="6" |Fluorine ICP: 3.8mT, 50/'''900W''', CHF3/CF4=10/30sccm, time='''210 sec''''
  
 
|-
  
|-
  +
|10/3/22
−
|Date
  
  +
|ND_FL_100322
−
|Sample#
  
  +
|228
−
|Etch Rate (nm/min)
  
  +
|1.10
−
|Etch Selectivity (SiO2/PR)
  
  +
|
−
|Averaged Sidewall Angle (<sup>o</sup>)
  
  +
|Low etch rate.
−
|SEM Image
  
  +
|[https://wiki.nanotech.ucsb.edu/w/images/8/8e/30D_10302022_FICP_002.jpg <nowiki>[30D]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/9/92/CS_10302022_FICP_002.jpg <nowiki>[CS]</nowiki>]
 
|-
  
|-
−
|11/5/2021
 +
|9/12/22
  +
|ND_FL_091222
−
|SOFL01
  
−
|136
 +
|278
−
|1.2
 +
|1.33
  +
|
  +
|high selectivity, may be
  +
due to new Si wafer
  +
|[https://wiki.nanotech.ucsb.edu/w/images/8/8e/30D_FICP_091222_002.jpg <nowiki>[30D]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/e/e7/CS_FICP_091222_002.jpg <nowiki>[CS]</nowiki>]
  +
|-
  +
|8/26/22
  +
|ND_FL_082622
  +
|288
  +
|0.97
  +
|
  +
|Low selectivity/e. rate
  +
|[https://wiki.nanotech.ucsb.edu/w/images/b/b9/30D_FICP_082622_001.jpg <nowiki>[30D]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/8/86/CS_FICP_082622_001.jpg <nowiki>[CS]</nowiki>]
  +
|-
  +
|8/22/22
  +
|ND_FL_082222
  +
|252.7
  +
|0.93
  +
|
  +
|Lower selectivity/e. rate
  +
|[https://wiki.nanotech.ucsb.edu/w/images/3/3d/40D_FICP_082222_001.jpg <nowiki>[40D]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/5/5b/CS_FICP_082222_002.jpg <nowiki>[CS]</nowiki>]
  +
|-
  +
|8/19/22
  +
|ND_Fl_081922
  +
|260.7
  +
|0.99
  +
|
  +
|Low selectivity/etch rate
  +
|[https://wiki.nanotech.ucsb.edu/w/images/8/82/30D_08192022_FICP_001.jpg <nowiki>[30D]</nowiki>][https://wiki.nanotech.ucsb.edu/w/images/5/56/CS_08192022_FICP_001.jpg <nowiki>[CS]</nowiki>]
  +
|-
  +
| colspan="7" |'''''Change in operator - SEMs below (by NP) are erroneously measured to the trench, instead of flat plane.'''''
  +
|-
  +
|5/18/22
  +
|NP_SiO2_Fl_10
  +
|308.7
  +
|1.19
  +
|
  +
|still lower etch rate
  +
|[https://wiki.nanotech.ucsb.edu/w/images/5/5d/SiO2_Fl_10_45D-003.jpg <nowiki>[1]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/0/06/SiO2_Fl_10_CS_007.jpg <nowiki>[2]</nowiki>]
  +
|-
  +
|5/10/22
  +
|NP_SiO2_Fl_09
  +
|307.3
  +
|1.15
  +
|
  +
|*etch rate seems lower*
  +
|[https://wiki.nanotech.ucsb.edu/w/images/a/a8/SiO2_Fl_09_45D_005.jpg <nowiki>[1]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/a/a7/SiO2_Fl_09_CS_006.jpg <nowiki>[2]</nowiki>]
  +
|-
  +
|4/26/22
  +
|NP_SiO2_Fl_08
  +
|344.7
  +
|1.4
  +
|
  +
|
  +
|[https://wiki.nanotech.ucsb.edu/w/images/c/c2/SiO2_Fl_08_45D_004.jpg <nowiki>[1]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/4/47/SiO2_Fl_08_CS_005.jpg <nowiki>[2]</nowiki>]
  +
|-
  +
|4/20/22
  +
|NP_SiO2_Fl_07
  +
|354.7
  +
|1.11
  +
|
  +
|
  +
|[https://wiki.nanotech.ucsb.edu/w/images/f/f5/SiO2_Fl_07_45D_003.jpg <nowiki>[1]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/3/34/SiO2_Fl_07_CS_004.jpg <nowiki>[2]</nowiki>]
  +
|-
  +
|4/14/22
  +
|NP_SiO2_Fl_06
  +
|352.7
  +
|1.11
  +
|
  +
|
  +
|[https://wiki.nanotech.ucsb.edu/w/images/7/70/SiO2_Fl_06_45D_002.jpg <nowiki>[1]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/6/68/SiO2_Fl_06_CS_002.jpg <nowiki>[2]</nowiki>]
  +
|-
  +
|3/29/22
  +
|NP_SiO2_Fl_05
  +
|334.7
  +
|1.07
  +
|
  +
|
  +
|[https://wiki.nanotech.ucsb.edu/w/images/a/a3/SiO2_Fl_03_45D_002.jpg <nowiki>[1]</nowiki>][https://wiki.nanotech.ucsb.edu/w/images/e/e2/SiO2_Fl_05_CS_002.jpg <nowiki>[2]</nowiki>]
  +
|-
  +
|3/09/22
  +
|NP_SiO2_Fl_04
  +
|358.9
  +
|1.06
  +
|
  +
|
  +
|[https://wiki.nanotech.ucsb.edu/w/images/f/f3/SiO2_FL_04_45D_001.jpg <nowiki>[1]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/d/db/SiO2_Fl_04_CS_005.jpg <nowiki>[2]</nowiki>]
  +
|-
  +
|3/02/22
  +
|NP_SiO2_Fl_03
  +
|347
  +
|1.05
  +
|
  +
|
  +
|[https://wiki.nanotech.ucsb.edu/w/images/b/b7/SiO2_Fl_03_45D_001.jpg <nowiki>[1]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/3/38/SiO2_Fl_03_CS_004.jpg <nowiki>[2]</nowiki>]
  +
|-
  +
|2/23/22
  +
|NP_SiO2_Fl_02
  +
|362.7
  +
|1.02
  +
|
 
|
  
|
−
|[https://wiki.nanotech.ucsb.edu/w/images/f/fe/SOFL0103.pdf]
 +
|[https://wiki.nanotech.ucsb.edu/w/images/c/c8/SiO2_Fl_02_45D_001.jpg <nowiki>[1]</nowiki>] [https://wiki.nanotech.ucsb.edu/w/images/8/89/SiO2_Fl_02_CS_001.jpg <nowiki>[2]</nowiki>]
 
|}
  
|}

Latest revision as of 15:03, 9 January 2023

Fluorine ICP: 3.8mT, 50/900W, CHF3/CF4=10/30sccm, time=90 sec
Date Sample # Etch Rate (nm/min) Etch Selectivity (SiO2/PR) Averaged Sidewalls Angle Observations/Notes SEM Images (45d, cross section)
01/09/23 ND_FL_010923 263.3 1.31 [30D][CS]
12/14/22 ND_FL_121422 266.7 1.29 [30D][CS]
12/09/22 ND_FL_120922 260 1.26 [30D][CS]
11/18/22 ND_FL_111822 268 1.01 [30D][CS]
11/07/22 ND_FL_110722 264.7 0.96 [30D] [CS]
10/24/22 ND_FL_102422 266.7 1.22 [30D][CS]
10/14/22 ND_FL_101422 249 0.82 Image drifted very slightly

in SEM. May account for

low selectivity.

[30D] [CS]
10/3/22 ND_FL_100322 228 1.10 Low etch rate. [30D] [CS]
9/12/22 ND_FL_091222 278 1.33 high selectivity, may be

due to new Si wafer

[30D] [CS]
8/26/22 ND_FL_082622 288 0.97 Low selectivity/e. rate [30D] [CS]
8/22/22 ND_FL_082222 252.7 0.93 Lower selectivity/e. rate [40D] [CS]
8/19/22 ND_Fl_081922 260.7 0.99 Low selectivity/etch rate [30D][CS]
Change in operator - SEMs below (by NP) are erroneously measured to the trench, instead of flat plane.
5/18/22 NP_SiO2_Fl_10 308.7 1.19 still lower etch rate [1] [2]
5/10/22 NP_SiO2_Fl_09 307.3 1.15 *etch rate seems lower* [1] [2]
4/26/22 NP_SiO2_Fl_08 344.7 1.4 [1] [2]
4/20/22 NP_SiO2_Fl_07 354.7 1.11 [1] [2]
4/14/22 NP_SiO2_Fl_06 352.7 1.11 [1] [2]
3/29/22 NP_SiO2_Fl_05 334.7 1.07 [1][2]
3/09/22 NP_SiO2_Fl_04 358.9 1.06 [1] [2]
3/02/22 NP_SiO2_Fl_03 347 1.05 [1] [2]
2/23/22 NP_SiO2_Fl_02 362.7 1.02 [1] [2]