Back to Lithography Recipes.

Below is a listing of stepper lithography recipes. Stepper 1 and Stepper 2 are i-line systems with good piece handling capabilities. Stepper 3 is a DUV (248nm) system primarily used for full 100mm wafers. DUV resists do not work for i-line and i-line resists do not work for DUV. Based on your sample reflectivity, absorption (or whether or not you use an ARC layer), and surface topography, the exposure time / focus offset parameters may vary.

This listing is a guideline to get you started. For critical lithography steps, you should run your own exposure and/or focus array to determine the proper parameters.

The recipes are tabulated to give you the values of the key parameters you will need to establish your recipe. Underlayers such as LOL2000 or PMGI can be used on the stepper systems. See the underlayer datasheets for details. Post develop bakes (not listed) are used to make the resist more etch resistant and depend on subsequent processes. Care should be taken with post development bakes as resist reflow can occur. Unless otherwise noted, all exposures are done on flat, silicon wafers.

Parameters are indicated in separate tables for each stepper system.

Stepper 1 (GCA 6300)

Multiply the GCA 6300 exposure times by 0.30 to get a starting exposure time for the GCA Autostep200 system.

Positive Resist (GCA 6300)

Unless otherwise noted, bakes are on hot plates. For recipes with CEM, the CEM is spun on after the first resist bake, exposure is then done, and the CEM is rinsed off with DI water before the PEB. CEM generally improves resolution and process tolerance at the expense of higher exposure time.

Resist	Spin Cond.	Bake	Thickness	Exposure Time	Focus Offset	PEB	Developer	Developer Time	Comments
SPR955CM0.9	3 krpm/30”	95°C/60”	~ 0.9 um	1.2”	0	110°C/60”	AZ300MIF	60"	0.5 um isolated lines See SPR955CM data file
SPR955CM0.9	3 krpm/30”	95°C/60”	~ 0.9 um	3.0”	4	110°C/60”	AZ300MIF	60"	0.5 um holes Much longer exposure time for dense isolated holes See SPR955CM data file
SPR955CM0.9 CEM365iS	3 krpm/30” 5 krpm/30”	95°C/90”	~ 0.9 um	2.2”	-10	110°C/60”	AZ300MIF	60"	0.35um isolated spaces by SEM measurement. Higher exposure time due to CEM See SPR955CM data file
SPR950-0.8	4 krpm/30”	95°C/60”	~ 0.8 um	1.0”	0	105°C/60”	AZ300MIF	60"
SPR955CM-1.8	4 krpm/30”	90°C/90”	~ 1.8 um	2.3”	0	110°C/90”	AZ300MIF	60"	0.5 um isolated lines See 955CM-1.8 data file
SPR955CM-1.8	4 krpm/30”	90°C/90”	~ 1.8 um	1.7”	-5	110°C/90”	AZ300MIF	60"	1 um isolated posts See 955CM-1.8 data file
SPR220-3.0	2.5 krpm/30”	115°C/90”	~ 2.7 um	2.4”	10	115°C/90”	AZ300MIF	60"	0.5 um isolated lines See SPR220-3 Data File
SPR220-7.0	3.5 krpm/45”	115°C/120”	~ 7.0 um	4.5”	0	*50°C/60” 115°C/90”	AZ300MIF	120"	1.0 um isolated lines; 1.25 um isolated spaces Let sample sit in air for 20 minutes before PEB, step to 50°C for 60” first, then 115°C See SPR220-7 Data File

Negative Resist (GCA 6300)

Unless otherwise noted, bakes are on hot plate. All flood exposures are done in broadband light using any contact aligner. Also, because the tone is negative, a shorter first exposure time will result in more undercut, which is desirable for single-layer lift-off processes. Under these conditions more develop time will also give more undercut.

Resist	Spin Cond.	Bake	Thickness	Exposure Time	Focus Offset	PEB	Flood	Developer	Developer Time	Comments
AZ5214	6 krpm/30”	95°C/60”	~ 1.0 um	0.2”	0	110°C/60”	60"	AZ300MIF	60"	0.7 um res. possible
nLOF5510	3 krpm/30”	90°C/60”	~ 0.93 um	0.74”	-6	110°C/60”	0	AZ300MIF	60"	0.5 um line openings good dense or isolated Use heated 1165 stripper for removal or lift-off See nLOF5510 data file
nLOF2020	4 krpm/30”	110°C/60”	~ 2 um	0.55”	-6	110°C/60”	0	AZ300MIF	90"	~ .85 um line opening/lift-off good. Isolated mesas can be smaller. Use heated 1165 stripper for removal or lift-off Sensetive to PEB temp. See nLOF2020 Data File

Stepper 2 (AutoStep 200)

Positive Resist (AutoStep 200)

Unless otherwise noted, bakes are on hot plates. For recipes with CEM, the CEM is spun on after the first resist bake, exposure is then done, and the CEM is rinsed off with DI water before the PEB. CEM generally improves resolution and process tolerance at the expense of higher exposure time.

NOTE: The bolded exposure times were found by multiplying the exposure times from the GCA 6300 system by 0.30. They should be sued as a starting point. You will need to do an exposure array to get precise times for the Autostep system. In general, the resolution achievable is ~ 100 nm smaller for the Autostep200 system.

Resist	Spin Cond.	Bake	Thickness	Exposure Time	Focus Offset	PEB	Developer	Developer Time	Comments
SPR955CM-0.9	3 krpm/30”	95°C/90”	~ 0.9 um	0.35”	0	110°C/90”	AZ300MIF	60”	0.5um dense lines See SPR955CM AS200 data file
SPR955CM-0.9	3 krpm/30”	95°C/90”	~ 0.9 um	0.8”	0	110°C/90”	AZ300MIF	60”	0.5um holes
SPR955CM-1.8	4 krpm/30”	95°C/90”	~ 1.8 um	0.4”	-1	110°C/90”	AZ300MIF	60”	See SPR955-1.8 AS200 data file
SPR950-0.8	4 krpm/30”	95°C/60”	~ 0.8 um	0.30”	0	105°C/60”	AZ300MIF	60"
SPR220-3.0	2.5 krpm/30”	115°C/90”	~ 2.7 um	0.72”	10	115°C/90”	AZ300MIF	60"	0.5 um isolated lines
SPR220-7.0	3.5 krpm/45”	115°C/120”	~ 7.0 um	1.35"	0	*50°C/60” 115°C/90”	AZ300MIF	120"	1.0 um isolated lines; 1.25 um isolated spaces Let sample sit in air for 20 minutes before PEB, step to 50°C for 60” first, then 115°C

Negative Resist (AutoStep 200)

Unless otherwise noted, bakes are on hot plate. All flood exposures are done in broadband light using any contact aligner. Also, because the tone is negative, a shorter first exposure time will result in more undercut, which is desirable for single-layer lift-off processes. Under these conditions more develop time will also give more undercut.

NOTE: The bolded exposure times were found by multiplying the exposure times from the GCA 6300 system by 0.30. They should be sued as a starting point. You will need to do an exposure array to get precise times for the Autostep system. In general, the resolution achievable is ~ 100 nm smaller for the Autostep200 system.

Resist	Spin Cond.	Bake	Thickness	Exposure Time	Focus Offset	PEB	Flood	Developer	Developer Time	Comments
nLOF5510	3 krpm/30”	90°C/60”	~ 0.93 um	.25”	-1	110°C/60”	0	AZ300MIF	60”	0.4 um lines dense good Use heated 1165 stripper for removal or lift-off See nLOF5510 As200 data file
AZ5214	6 krpm/30”	95°C/60”	~ 1.0 um	0.06”	0	110°C/60”	60"	AZ300MIF	60"	0.7 um res. possible
nLOF2020	4 krpm/30”	110°C/60”	~ 2 um	0.17”	-6	110°C/60”	0	AZ300MIF	90"	~ .85 um line opening/lift-off good. Isolated mesas can be smaller. Use heated 1165 stripper for removal or lift-off Sensetive to PEB temp.
NR9-1000PY	3 krpm/30”	135°C/180” lid down	~ 1.2 um	0.92”	0	115°C/120” lid down	0	AZ300MIF	20"	~ .55 um line opening/lift-off good. Use heated 1165 stripper for removal 8Hrs min. See NR9-1000PY As200 data file

Stepper 3 (ASML DUV)

Anti-Reflective Coatings

Anti-reflective coatings (aka. ARC or AR Coating) are, in general, used for the ASML stepper. LOL2000 and PMGI can also be used as under layers.

DUV-42P

(replacement for AR2)

spin coat at 3500rpm for a 670Å thick coating.
Bake at 220°C for 60s on a hotplate.
This AR coating is removed via oxygen plasma.
This ARC can be etched on ICP#1, ICP#2 or RIE#5
Datasheet: DUV-42P

DS-K101-304

spin at 5000rpm and bake at 185C for 60s.
- ~20nm thickness
This AR coating develops away and undercuts in AZ300MIF.
- For isolated lines, this can cause them to lift-off by undercutting the resist.
Increase bake temperature to reduce undercut rate.
- DS-K101-304 Bake Temp. versus Develop Rate - Click for experimental data
- Can be used similarly to DUV42P (dry etch removal) by baking at 220°C.
Datasheet: DS-K101-304

Positive Resist (ASML DUV)

Please see section above for anti-reflection coatings, which are usually used with the DUV Stepper.

Resist	Spin Cond.	Bake	Thickness	Exposure Dose(mj)	Focus Offset	PEB	Developer	Developer Time	Comments
UV6-0.7 (replaced by UV6-0.8)	3.5 krpm/30”	135°C/60”	630nm	17	-0.2	135°C/90”	AZ300MIF	45”	200nm dense line/space NA 0.57, Sigma 0.75 Eo ~ 5.5mj UV6-0.7 was discontinued, we now stock UV6-0.8
UV210-0.3	5.0 krpm/30”	135°C/60”	230nm	20	-0.1	135°C/90”	AZ300MIF	45"	150nm dense line/space Annular Illumination NA 0.63, Sigma_o 0.8, Sigma_i 0.5
UV210-0.3	3.0 krpm/30”	135°C/90”	260nm	85	-0.2	135°C/90”	AZ300MIF	80”	170nm isolated holes Annular Illumination NA 0.63, Sigma_o 0.8, Sigma_i 0.5

Negative Resist (ASML DUV)