{| class="wikitable sortable"
  
{| class="wikitable sortable"
 
|-
  
|-
−
! Material !! P(mT) !! Pow(W) !! Sub(W) !! T(C) !! Ar !! N2 !! O2 !! Height-Tilt !! Rate(nm/min) !! Stress(MPa) !! Rs(uOhm-cm) !! n@633nm !! k@633nm !! Data Below !! Comment
 +
!Material!!P(mT)!!Pow(W)!!Sub(W)!!T(C)!!Ar!!N2!!O2!!Height-Tilt!!Rate(nm/min)!!Stress(MPa)!!Rs(uOhm-cm)!!n@633nm!!k@633nm
  +
!Target Consumed Lower Limit!!Data Below!!Comment
  +
|-
  +
|Au
  +
| -
  +
| -
  +
| -
  +
| -
  +
| -
  +
| -
  +
| -
  +
| -
  +
| -
  +
| -
  +
| -
  +
| -
  +
| -
  +
|Set: 200 W
  +
Read: 400 VDC
  +
|no
  +
|
 
|-
  
|-
 
|Al2O3
  
|Al2O3
Line 24: Line 44:
 
|1.6478
  
|1.6478
 
|0
  
|0
  +
|
 
|no
  
|no
 
|Demis D. John
  
|Demis D. John
 
|-
  
|-
−
| Co || 10(5) || 200 || 0 || 20 || 25 || 0 || 0 || 25-9 || 2.3 || - || - || - || - || yes || Alex K
 +
|Co||10(5)||200||0||20||25||0||0||25-9||2.3||-||-||-||-
  +
| ||yes||Alex K
 
|-
  
|-
−
| Cr || 5 || 200 || 0 || 20 || 25 || 0 || 0 || 44-4 || 6.84 || - || - || - || - || no || Brian
 +
|Cr||5||200||0||20||25||0||0||44-4||6.84||-||-||-||-
  +
| ||no||Brian
 
|-
  
|-
−
| Cu || 1.5 || 50(395v) || 0 || 20 || 25 || 0 || 0 || 25-9 || 4.15 || - || - || - || - || no || Ning
 +
|Cu||1.5||50(395v)||0||20||25||0||0||25-9||4.15||-||-||-||-
  +
| ||no||Ning
 
|-
  
|-
−
| Cu || 5 || 150(~490v) || 0 || 20 || 15 || 0 || 0 || 0.82"-9 || 8 || - || - || - || - || yes || Ning
 +
|Cu||5||150(~490v)||0||20||15||0||0||0.82"-9||8||-||-||-||-
  +
| ||yes||Ning
 
|-
  
|-
−
| Fe || 10(5) || 200 || 0 || 20 || 25 || 0 || 0 || 25-9 || 1.25 || - || - || - || - || No || Alex K
 +
|Fe||10(5)||200||0||20||25||0||0||25-9||1.25||-||-||-||-
  +
| ||No||Alex K
 
|-
  
|-
−
| Mo || 3 || 200 || 0 || 20 || 25 || 0 || 0 || 44-4 || 13.15 || - || - || - || - || yes || Ning
 +
|Mo||3||200||0||20||25||0||0||44-4||13.15||-||-||-||-
  +
| ||yes||Ning
 
|-
  
|-
−
| Ni || 5 || 150 || 0 || 20 || 25 || 0 || 0 || 44-4 || 5.23 || - || - || - || - || yes || Ning
 +
|Ni||5||150||0||20||25||0||0||44-4||5.23||-||-||-||-
  +
| ||yes||Ning
 
|-
  
|-
−
| Ni || 5 || 150 || 0 || 20 || 25 || 0 || 0 || 25-9 || 1.82 || - || - || - || - || yes || Ning
 +
|Ni||5||150||0||20||25||0||0||25-9||1.82||-||-||-||-
  +
| ||yes||Ning
 
|-
  
|-
−
| Ni || 5 || 75 || 0 || 20 || 25 || 0 || 0 || 44-4 || 2.50 || - || - || - || - || yes || Ning
 +
|Ni||5||75||0||20||25||0||0||44-4||2.50||-||-||-||-
  +
| ||yes||Ning
 
|-
  
|-
−
| Ni || 3 || 200 || 0 || 20 || 25 || 0 || 0 || 44-4 || 9.4 || - || - || - || - || yes || Ning
 +
|Ni||3||200||0||20||25||0||0||44-4||9.4||-||-||-||-
  +
| ||yes||Ning
 
|-
  
|-
−
| Ni || 1.5 || 50(399v) || 0 || 20 || 25 || 0 || 0 || 25-9 || 0.96 || - || - || - || - || no || Ning
 +
|Ni||1.5||50(399v)||0||20||25||0||0||25-9||0.96||-||-||-||-
  +
| ||no||Ning
 
|-
  
|-
−
| Pt || 3 || 50 || 0 || 20 || 25 || 0 || 0 || 25-9 || 4.1 || - || - || - || - || no|| Ning
 +
|Pt||3||50||0||20||25||0||0||0.82"-9||2.9||-||-||-||-
  +
| ||no||Ning
 
|-
  
|-
−
| Si || 8 || 250 || 0 || 25 || 25 || 0 || 0 || 15-3 || 1.4 || - || - || - || - || no || Gerhard - ramp 2W/s - 3% Unif 4" wafer
 +
|Si||8||250||0||25||25||0||0||15-3||1.4||-||-||-||-
  +
| ||no||Gerhard - ramp 2W/s - 3% Unif 4" wafer
 
|-
  
|-
−
| SiN || 3 || 200 || 10 || 20 || 25 || 3 || 0 || 25-9 || 1.56 || - || - || 1.992 || - || yes || Brian
 +
|SiN||3||200||10||20||25||3||0||25-9||1.56||-||-||1.992||-
  +
| ||yes||Brian
 
|-
  
|-
−
| SiN || 3 || 250 || 10 || 20 || 25 || 2.5 || 0 || 25-9 || 2.1 || - || - || 2.06 || - || yes || Brian
 +
|SiN||3||250||10||20||25||2.5||0||25-9||2.1||-||-||2.06||-
  +
| ||yes||Brian
 
|-
  
|-
−
| SiO2 || 3 || 200 || 10 || 20 || 25 || 0 || 3 || 25-9 || 3.68 || - || - || 1.447 || - || yes || Brian
 +
|SiO2||3||200||10||20||25||0||3||25-9||3.68||-||-||1.447||-
  +
| ||yes||Brian
 
|-
  
|-
−
| SiO2 || 3 || 200 || 10 || 20 || 25 || 0 || 5 || 45-3 || 2.60 || - || - || 1.471 || - || yes || Brian
 +
|SiO2||3||200||10||20||25||0||5||45-3||2.60||-||-||1.471||-
  +
| ||yes||Brian
 
|-
  
|-
−
| SiO2 || 3 || 250 || 10 || 20 || 25 || 0 || 2.5 || 25-9 || 4.3 || - || - || 1.485 || - || yes || Brian
 +
|SiO2||3||250||10||20||25||0||2.5||25-9||4.3||-||-||1.485||-
  +
| ||yes||Brian
 
|-
  
|-
−
| Ta || 5 || 150 || 0 || 20 || 25 || 0 || 0 || 44-4 || 9.47 || - || - || - || - || yes || Ning
 +
|Ta||5||150||0||20||25||0||0||44-4||9.47||-||-||-||-
  +
| ||yes||Ning
 
|-
  
|-
−
| Ta || 5 || 75 || 0 || 20 || 25 || 0 || 0 || 44-4 || 5.03 || - || - || - || - || yes || Ning
 +
|Ta||5||75||0||20||25||0||0||44-4||5.03||-||-||-||-
  +
| ||yes||Ning
 
|-
  
|-
−
| Ti || 3 || 100 || 0 || 20 || 25 || 0 || 0 || 25-9 || 1.34 || - || - || - || - || yes || Ning
 +
|Ti||3||100||0||20||25||0||0||25-9||1.34||-||-||-||-
  +
| ||yes||Ning
 
|-
  
|-
−
| SampleClean-NativeSiO2 || 10 || 0 || 18 || 20 || 25 || 0 || 0 || 44-4 || - || - || - || - || - || yes || 150Volts 5 min
 +
|SampleClean-NativeSiO2||10||0||18||20||25||0||0||44-4||-||-||-||-||-
  +
| ||yes||150Volts 5 min
 
|-
  
|-
 
|}
  
|}
   
−
== Height Conversion for Older Recipes ==
 +
==Height Conversion for Older Recipes==
 
Old recipes using the manual Height setting in millimeters can be converted to the new programmatic settings in inches as follows:
  
Old recipes using the manual Height setting in millimeters can be converted to the new programmatic settings in inches as follows:
 
{| class="wikitable"
  
{| class="wikitable"
Line 94: Line 137:
 
Interpolation plot [[:File:Sputter 3 - height conversion v1.PNG|can be found here.]]
  
Interpolation plot [[:File:Sputter 3 - height conversion v1.PNG|can be found here.]]
   
−
== Fe and Co Deposition (Sputter 3) ==
 +
==Fe and Co Deposition (Sputter 3)==
−
*[[media:Fe and Co Films using Sputter-3.pdf|Fe and Co Deposition Recipe]]
  
−
== Cu Deposition (Sputter 3) ==
  
−
*[[media:Cu Film using Sputter-3.pdf|Cu Deposition Recipe]]
  
   
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/1/15/Fe_and_Co_Films_using_Sputter-3.pdf Fe and Co Deposition Recipe]
−
== Mo Deposition (Sputter 3) ==
  
−
*[[media:46-Mo Film using Sputter3.pdf|Mo Deposition Recipe]]
  
   
−
== Ni and Ta Deposition (Sputter 3) ==
 +
==Cu Deposition (Sputter 3)==
−
*[[media:24-Ni and Ta Films using Sputter-3.pdf|Ni and Ta Deposition Recipe]]
  
−
*[[media:Ni Sputtering Film using Sputter 3-a.pdf|Ni Sputtering Film Recipe-3mT-200W]]
  
   
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/5/5e/Cu_Film_using_Sputter-3.pdf Cu Deposition Recipe]
−
== SiO2 Deposition (Sputter 3) ==
  
−
*[[media:SiO2-AJA-1-Reactive-Sputter-Uniformity-rev-1.pdf|SiO2 Uniformity Data]]
  
−
*[[media:SiO2-AJA-1-Reactive-Sputter-Power-Flow-AFM-Roughness-rev1.pdf|SiO2 Flow and Bias Variations Including AFM Data]]
  
   
−
== SiN Deposition (Sputter 3) ==
 +
==Mo Deposition (Sputter 3)==
−
*[[media:SiN-AJA-1-Reactive-Sputtering-Power-Flow-AFM-Rate-Index-rev1.pdf|SiN Flow and RF Variations Including AFM Data]]
  
   
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/7/7f/46-Mo_Film_using_Sputter3.pdf Mo Deposition Recipe]
−
== Ti Deposition (Sputter 3) ==
  
  +
−
*[[media:Ti Sputtering Film using Sputter 3.pdf|Ti Sputtering Film Recipe-3mT-100W]]
  
  +
==Ni and Ta Deposition (Sputter 3)==
  +
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/b/b6/24-Ni_and_Ta_Films_using_Sputter-3.pdf Ni and Ta Deposition Recipe]
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/9/93/Ni_Sputtering_Film_using_Sputter_3-a.pdf Ni Sputtering Film Recipe-3mT-200W]
  +
  +
==SiO2 Deposition (Sputter 3)==
  +
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/e/ef/SiO2-AJA-1-Reactive-Sputter-Uniformity-rev-1.pdf SiO2 Uniformity Data]
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/b/b2/SiO2-AJA-1-Reactive-Sputter-Power-Flow-AFM-Roughness-rev1.pdf SiO2 Flow and Bias Variations Including AFM Data]
  +
  +
==SiN Deposition (Sputter 3)==
  +
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/f/fb/SiN-AJA-1-Reactive-Sputtering-Power-Flow-AFM-Rate-Index-rev1.pdf SiN Flow and RF Variations Including AFM Data]
  +
  +
==Ti Deposition (Sputter 3)==
  +
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/3/3b/Ti_Sputtering_Film_using_Sputter_3.pdf Ti Sputtering Film Recipe-3mT-100W]
   
 
=[[Sputter 4 (AJA ATC 2200-V)]]=
  
=[[Sputter 4 (AJA ATC 2200-V)]]=
Line 122: Line 173:
 
{| class="wikitable sortable"
  
{| class="wikitable sortable"
 
|-
  
|-
−
! Material !! P(mT)
+
!Material!!P(mT)
−
!Power Source!! Pow(W) !! Sub(W) !! T(C) !! Ar !! N2 !! O2 !! Height-Tilt !! Rate(nm/min) !! Stress(MPa) !! Rs(uOhm-cm) !! n@633nm !! k@633nm !! Data Below !! Comment
 +
!Power Source!!Pow(W)!!Sub(W)!!T(C)!!Ar!!N2!!O2!!Height-Tilt!!Rate(nm/min)!!Stress(MPa)!!Rs(uOhm-cm)!!n@633nm!!k@633nm!!Data Below!!Comment
 
|-
  
|-
−
| Al || 5
+
|Al||5
−
||| 200 || 0 || 20 || 45 || 0 || 0 || H2.75-T5 || 4.4 || - || - || - || - || Yes || Ning Cao
+
| ||200||0||20||45||0||0||H2.75-T5||4.4||-||-||-||-||Yes||Ning Cao
 
|-
  
|-
 
|Al2O3
  
|Al2O3
Line 146: Line 197:
 
|Demis D. John
  
|Demis D. John
 
|-
  
|-
−
| Au || 5
+
|Au||5
−
||| 200 || 0 || 20 || 45 || 0 || 0 || H1-T10 || 17.7 || - || - || - || - || Yes || Ning Cao
 +
| ||200||0||20||45||0||0||H1-T10||17.7||-||-||-||-||Yes||Ning Cao
 
|-
  
|-
−
| Au || 10
+
|Au||10
−
||| 300 || 0 || 20 || 45 || 0 || 0 || H2.75-T5 || 45.4 || - || - || - || - || Yes || Ning Cao
 +
| ||300||0||20||45||0||0||H2.75-T5||45.4||-||-||-||-||Yes||Ning Cao
 
|-
  
|-
 
|Cu
  
|Cu
Line 170: Line 221:
 
|Ning Cao
  
|Ning Cao
 
|-
  
|-
−
| Nb || 4
+
|Nb||4
−
||| 250 || 0 || 20 || 30 || 0 || 0 || H2.00-T7 || 7.5 || - || - || - || - || No ||
+
| ||250||0||20||30||0||0||H2.00-T7||7.5||-||-||-||-||No||
 
|-
  
|-
−
| Pt || 5
+
|Pt||5
−
||| 200 || 0 || 20 || 45 || 0 || 0 || H2.75-T5 || 7.4 || - || - || - || - || Yes || Ning Cao
+
| ||200||0||20||45||0||0||H2.75-T5||7.4||-||-||-||-||Yes||Ning Cao
 
|-
  
|-
−
| Pt || 3
+
|Pt||3
−
||| 50(439V) || 0 || 20 || 45 || 0 || 0 || H2.75-T5 || 3.9 || - || - || - || - || Yes || Ning Cao
 +
| ||50(439V)||0||20||45||0||0||H2.75-T5||3.9||-||-||-||-||Yes||Ning Cao
 
|-
  
|-
−
| Ti || 10
+
|Ti||10
−
||| 200 || 0 || 20 || 45 || 0 || 0 || H2.75-T5 || 2.3 || - || - || - || - || Yes || Ning Cao
 +
| ||200||0||20||45||0||0||H2.75-T5||2.3||-||-||-||-||Yes||Ning Cao
 
|-
  
|-
−
| TiN || 3
+
|TiN||3
−
||| 150 || 110V || 20 || 48.25 || 1.75 || 0 || H2.5-T5 || 2 || - || 60 || - || - || No ||
+
| ||150||110V||20||48.25||1.75||0||H2.5-T5||2||-||60||-||-||No||
 
|-
  
|-
−
| TiO<sub>2</sub> || 3
+
|TiO<sub>2</sub>||3
−
||| 250(RF:450V) || 0 || 20 || 45 || 0 || 3 || H2.75-T5 ||4.3|| - || || - || - || Yes || Ning Cao
+
| ||250(RF:450V)||0||20||45||0||3||H2.75-T5||4.3||-|| ||-||-||Yes||Ning Cao
 
|-
  
|-
−
| TiW || 4.5
+
|TiW||4.5
−
||| 200 || 0 || 20 || 45 || 0 || 0 || H1-T10 || 4.7 || - || - || - || - || Yes || Ning Cao
 +
| ||200||0||20||45||0||0||H1-T10||4.7||-||-||-||-||Yes||Ning Cao
 
|-
  
|-
−
| TiW || 4.5
+
|TiW||4.5
−
||| 300 || 0 || 75 || 45 || 0 || 0 || H2.75-T5 || 9.5 || -150 to 150 || 60 || - || - || Yes || 10%Ti by Wt
 +
| ||300||0||75||45||0||0||H2.75-T5||9.5||-150 to 150||60||-||-||Yes||10%Ti by Wt
 
|-
  
|-
−
| W || 3
+
|W||3
−
||| 300 || 0 || 50 || 45 || 0 || 0 || H2.75-T5 || 11.5 || -150 to 150 || 11 || - || - || Yes || Jeremy Watcher
+
| ||300||0||50||45||0||0||H2.75-T5||11.5||-150 to 150||11||-||-||Yes||Jeremy Watcher
 
|-
  
|-
   
 
|}
  
|}
−
== W-TiW Deposition (Sputter 4) ==
 +
==W-TiW Deposition (Sputter 4)==
−
*[[media:W-TiW-Sputtering-AJA-4-Data-Recipe-RevB.pdf|W-TiW Deposition Recipe]]
  
   
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/c/cc/W-TiW-Sputtering-AJA-4-Data-Recipe-RevB.pdf W-TiW Deposition Recipe]
−
== Ti-Au Deposition (Sputter 4) ==
  
−
*[[media:Ti-Au-Sputtering-Films-AJA2-rev1.pdf|Ti-Au Deposition Recipe and SEM Cross-Sections]]
  
   
−
== Pt Deposition (Sputter 4) ==
 +
==Ti-Au Deposition (Sputter 4)==
−
*[[media:Pt-Sputter4.pdf|Pt Film's AFM Step and Roughness]]
  
   
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/8/89/Ti-Au-Sputtering-Films-AJA2-rev1.pdf Ti-Au Deposition Recipe and SEM Cross-Sections]
−
== TiW Deposition (Sputter 4) ==
  
−
*[[media:TiW-Sputter4-4.5mT-300W-300s.pdf|TiW Film's AFM Step and Roughness]]
  
   
−
== TiO<sub>2</sub> Deposition (Sputter 4) ==
 +
==Pt Deposition (Sputter 4)==
−
*[[media:TiO2 film using Sputter4.pdf|TiO<sub>2</sub> Film's Refractive Index Spectrum, Resistivity, AFM Roughness]]
  
   
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/a/ab/Pt-Sputter4.pdf Pt Film's AFM Step and Roughness]
−
== Au Deposition (Sputter 4) ==
  
−
*[[media:Au-Sputter4-5mT-200W-120s.pdf|Au Film's AFM Step and Roughness]]
  
   
−
== Al Deposition (Sputter 4) ==
 +
==TiW Deposition (Sputter 4)==
−
*[[media:Al-Sputter4-5mT-200W-30m.pdf|Al Film SEM Profile]]
  
   
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/7/78/TiW-Sputter4-4.5mT-300W-300s.pdf TiW Film's AFM Step and Roughness]
−
== Al2O3 Deposition (Sputter 4) ==
  
  +
−
* Rate: 5.134 nm/min
  
  +
==TiO<sub>2</sub> Deposition (Sputter 4)==
−
* [https://en.wikipedia.org/wiki/Cauchy%27s_equation Cauchy] Refractive Index Params (fit from λ=190-1700nm, indicating transparency over this range)
  
  +
−
** A = 1.626
  
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/1/19/TiO2_film_using_Sputter4.pdf TiO<sub>2</sub> Film's Refractive Index Spectrum, Resistivity, AFM Roughness]
−
** B = 5.980E-3
  
  +
−
** C = 1.622E-4
  
  +
==Au Deposition (Sputter 4)==
  +
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/0/01/Au-Sputter4-5mT-200W-120s.pdf Au Film's AFM Step and Roughness]
  +
  +
==Al Deposition (Sputter 4)==
  +
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/1/17/Al-Sputter4-5mT-200W-30m.pdf Al Film SEM Profile]
  +
  +
==Al2O3 Deposition (Sputter 4)==
  +
  +
*Rate: 5.134 nm/min
  +
*[https://en.wikipedia.org/wiki/Cauchy%27s_equation Cauchy] Refractive Index Params (fit from λ=190-1700nm, indicating transparency over this range)
  +
**A = 1.626
  +
**B = 5.980E-3
  +
**C = 1.622E-4
   
 
=[[Sputter 5 (AJA ATC 2200-V)]]=
  
=[[Sputter 5 (AJA ATC 2200-V)]]=
Line 234: Line 293:
 
{| class="wikitable sortable"
  
{| class="wikitable sortable"
 
|-
  
|-
−
! Material !! P(mT)
+
!Material!!P(mT)
−
!Power Source!! Pow(W) !! Sub(V) !! T(C) !! Ar !! N2 !! O2 !! Height-Tilt !! Rate(nm/min) !! Stress(MPa) !! Rs(uOhm-cm) !! Rq(nm)!! n@633nm !! k@633nm !! LPDb/LPDa*!! Data Below !! Comment
 +
!Power Source!!Pow(W)!!Sub(V)!!T(C)!!Ar!!N2!!O2!!Height-Tilt!!Rate(nm/min)!!Stress(MPa)!!Rs(uOhm-cm)!!Rq(nm)!!n@633nm!!k@633nm!!LPDb/LPDa*!!Data Below!!Comment
 
|-
  
|-
 
|Al
  
|Al
Line 277: Line 336:
 
|Demis 2018-04-13
  
|Demis 2018-04-13
 
|-
  
|-
−
| SiO2 || 3
+
|SiO2||3
−
||| 250 || 120 || 20 || 45 || 0 || 2 || H1.0-T10 || 2.32 || || - || - ||1.49 || - || 153/6384 || No || Biljana
+
| ||250||120||20||45||0||2||H1.0-T10||2.32|| ||-||-||1.49||-||153/6384||No||Biljana
 
|-
  
|-
−
| SiO2 || 3
+
|SiO2||3
−
||| 250 || 120 || 20 || 45 || 0 || 4.5 || H1.0-T10 || 2.29 || -515 || - || 0.210 || 1.49 || || 138/4445 || No ( AFM available) || Biljana
 +
| ||250||120||20||45||0||4.5||H1.0-T10||2.29||-515||-||0.210||1.49|| ||138/4445||No ( AFM available)||Biljana
 
|-
  
|-
−
| SiO2 || 3
+
|SiO2||3
−
||| 250 || 120 || 20 || 45 || 0 || 6 || H1.0-T10 || 2.32|| || - || - || 1.49 || - || 27/1515 || Yes || Biljana
 +
| ||250||120||20||45||0||6||H1.0-T10||2.32|| ||-||-||1.49||-||27/1515||Yes||Biljana
 
|-
  
|-
 
|}
  
|}
 
''*LPD: light particle detection:''
  
''*LPD: light particle detection:''
  +
 
*''LPDb: light particle detection before deposition''
  
*''LPDb: light particle detection before deposition''
 
*''LPDa: light particle detection after deposition''
  
*''LPDa: light particle detection after deposition''
  +
−
== SiO2 Deposition (Sputter 5) ==
  
  +
==SiO2 Deposition (Sputter 5)==
  +
 
*[https://docs.google.com/spreadsheets/d/1kzrbXdUJNf_-FjLJd-PTrbGDhGCKNNxo_JaOXkSpAF8/edit#gid=Sputter#5 SiO2 film]
  
*[https://docs.google.com/spreadsheets/d/1kzrbXdUJNf_-FjLJd-PTrbGDhGCKNNxo_JaOXkSpAF8/edit#gid=Sputter#5 SiO2 film]
   
Line 296: Line 358:
   
 
*[https://docs.google.com/spreadsheet/ccc?key=0AuBs1GfMrpnXcEdXanZQNko3X0lUcHhVUlNyYnVDUkE&usp=sharing IBD Calibrations Spreadsheet] - Records of historical film depositions (rates, indices), Uniformity etc.
  
*[https://docs.google.com/spreadsheet/ccc?key=0AuBs1GfMrpnXcEdXanZQNko3X0lUcHhVUlNyYnVDUkE&usp=sharing IBD Calibrations Spreadsheet] - Records of historical film depositions (rates, indices), Uniformity etc.
−
**'''All users are required to enter their calibration deps (simple test deps only)'''
+
**'''All users are required to enter their calibration deps (simple test deps only)'''
 
*[https://docs.google.com/spreadsheets/d/1y704PRxvXf8bbqb79CrISnk2t0FeojYVJIjrAcBU2_w/edit#gid=sharing Particulates in SiO2 and Ta2O5 in 2015]
  
*[https://docs.google.com/spreadsheets/d/1y704PRxvXf8bbqb79CrISnk2t0FeojYVJIjrAcBU2_w/edit#gid=sharing Particulates in SiO2 and Ta2O5 in 2015]
   
 
==SiO{{sub|2}} deposition (IBD)==
  
==SiO{{sub|2}} deposition (IBD)==
  +
−
*[[media: New IBD SiO2 Standard Recipe.pdf |SiO<sub>2</sub> Standard Recipe]]
  
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/8/8d/New_IBD_SiO2_Standard_Recipe.pdf SiO<sub>2</sub> Standard Recipe]
 
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dFRJLUZUdXB4WFA1S1BMMWQ4WndpTWc&usp=drive_web#gid=sharing SiO<sub>2</sub> Data December 2014]
  
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dFRJLUZUdXB4WFA1S1BMMWQ4WndpTWc&usp=drive_web#gid=sharing SiO<sub>2</sub> Data December 2014]
 
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dGNyV083bmpzMjZpZ0JFVWhoOUpaN3c#gid=sharing SiO<sub>2</sub> Thickness uniformity 2014]
  
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dGNyV083bmpzMjZpZ0JFVWhoOUpaN3c#gid=sharing SiO<sub>2</sub> Thickness uniformity 2014]
Line 310: Line 373:
 
*[https://docs.google.com/spreadsheets/d/1dFI1B2WxS7oEGMPl2dlLtmiAin-6EKWSEj9hFezB4_w/edit#gid==sharing SiO<sub>2</sub> Thickness uniformity-1hr depositions 2016]
  
*[https://docs.google.com/spreadsheets/d/1dFI1B2WxS7oEGMPl2dlLtmiAin-6EKWSEj9hFezB4_w/edit#gid==sharing SiO<sub>2</sub> Thickness uniformity-1hr depositions 2016]
   
−
====== SiO2 1hr deposition properties: ======
 +
======SiO2 1hr deposition properties:======
  +
 
*Dep.rate: ≈ 5.2 nm/min (users must calibrate this prior to critical deps)
  
*Dep.rate: ≈ 5.2 nm/min (users must calibrate this prior to critical deps)
 
*HF e.r.~350 nm/min
  
*HF e.r.~350 nm/min
Line 316: Line 380:
 
*Refractive Index: ≈ 1.494
  
*Refractive Index: ≈ 1.494
 
*[[http://en.wikipedia.org/wiki/Cauchy's_equation Cauchy Parameters]] (350-2000nm):
 
*[[http://en.wikipedia.org/wiki/Cauchy's_equation Cauchy Parameters]] (350-2000nm):
−
** A = 1.480
 +
**A = 1.480
−
** B = 0.00498
 +
**B = 0.00498
−
** C = -3.2606e-5
 +
**C = -3.2606e-5
  +
 
==Si<sub>3</sub>N<sub>4</sub> deposition (IBD)==
  
==Si<sub>3</sub>N<sub>4</sub> deposition (IBD)==
  +
−
*[[media:IBD SiNdeposition.pdf|Si<sub>3</sub>N<sub>4</sub> Standard Recipe]]
  
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/d/d3/IBD_SiNdeposition.pdf Si<sub>3</sub>N<sub>4</sub> Standard Recipe]
 
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dDE4RldRQnA1N1ptOUlHQVc3QjNXSkE#gid=sharing Si<sub>3</sub>N<sub>4</sub> Data December 2014]
  
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dDE4RldRQnA1N1ptOUlHQVc3QjNXSkE#gid=sharing Si<sub>3</sub>N<sub>4</sub> Data December 2014]
 
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dEdsbWRhYW9mbFRLem56TjFFWjRwR1E#gid=sharing Si<sub>3</sub>N<sub>4</sub> Thickness uniformity 2014]
  
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dEdsbWRhYW9mbFRLem56TjFFWjRwR1E#gid=sharing Si<sub>3</sub>N<sub>4</sub> Thickness uniformity 2014]
Line 329: Line 395:
 
*Refractive Index: ≈ 1.969
  
*Refractive Index: ≈ 1.969
 
*[[http://en.wikipedia.org/wiki/Cauchy's_equation Cauchy Parameters]] (350-2000nm):
 
*[[http://en.wikipedia.org/wiki/Cauchy's_equation Cauchy Parameters]] (350-2000nm):
−
** A = 2.000
 +
**A = 2.000
−
** B = 0.01974
 +
**B = 0.01974
−
** C = 1.2478e-4
 +
**C = 1.2478e-4
   
−
== SiO<sub>x</sub>N<sub>y</sub> deposition (IBD) ==
 +
==SiO<sub>x</sub>N<sub>y</sub> deposition (IBD)==
 
These are some old (2010), initial characterizations only. A recipe improvement would be to increase the Assist O2+N2 = 60sccm total, increasing repeatability. Contact [[Demis D. John|Demis]] for more info.
  
These are some old (2010), initial characterizations only. A recipe improvement would be to increase the Assist O2+N2 = 60sccm total, increasing repeatability. Contact [[Demis D. John|Demis]] for more info.
 
{|
  
{|
Line 342: Line 408:
 
==Ta{{sub|2}}O{{sub|5}} deposition (IBD)==
  
==Ta{{sub|2}}O{{sub|5}} deposition (IBD)==
   
−
*[[media:IBD Ta2O5 deposition details.pdf|Ta{{sub|2}}O{{sub|5}} Standard Recipe]]
 +
*[//wiki.nanotech.ucsb.edu/wiki/images/8/85/IBD_Ta2O5_deposition_details.pdf Ta{{sub|2}}O{{sub|5}} Standard Recipe]
 
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dGhhUGdCR2JudkZJU3pBemR4bS1GWWc#gid=0=sharing Ta{{sub|2}}O{{sub|5}} Data December 2014]
  
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dGhhUGdCR2JudkZJU3pBemR4bS1GWWc#gid=0=sharing Ta{{sub|2}}O{{sub|5}} Data December 2014]
 
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dE5xbVFyUFZqdTdUN0JRSUNvMGFGb2c#gid=sharing Ta{{sub|2}}O{{sub|5}} Thickness uniformity 2014]
  
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dE5xbVFyUFZqdTdUN0JRSUNvMGFGb2c#gid=sharing Ta{{sub|2}}O{{sub|5}} Thickness uniformity 2014]
Line 360: Line 426:
 
*Refractive Index: ≈ 2.172
  
*Refractive Index: ≈ 2.172
 
*[[http://en.wikipedia.org/wiki/Cauchy's_equation Cauchy Parameters]] (350-2000nm):
 
*[[http://en.wikipedia.org/wiki/Cauchy's_equation Cauchy Parameters]] (350-2000nm):
−
** A = 2.1123
 +
**A = 2.1123
−
** B = 0.018901
 +
**B = 0.018901
−
** C = -0.016222
 +
**C = -0.016222
   
 
==TiO{{sub|2}} deposition (IBD)==
  
==TiO{{sub|2}} deposition (IBD)==
  +
−
*[[media:New IBD TiO2 deposition.pdf|TiO<sub>2</sub> Standard Recipe]]
  
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/3/3b/New_IBD_TiO2_deposition.pdf TiO<sub>2</sub> Standard Recipe]
 
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dGVXVkM4dEdXaU15M09HNGhJbGUycVE#gid=sharing TiO<sub>2</sub> Data December 2014]
  
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dGVXVkM4dEdXaU15M09HNGhJbGUycVE#gid=sharing TiO<sub>2</sub> Data December 2014]
 
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dF9YSW9jTDJzY19MbmVEbUQtVzJVdVE#gid=sharing TiO<sub>2</sub> Thickness uniformity 2014]
  
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dF9YSW9jTDJzY19MbmVEbUQtVzJVdVE#gid=sharing TiO<sub>2</sub> Thickness uniformity 2014]
Line 374: Line 441:
 
*Refractive Index: ≈ 2.259
  
*Refractive Index: ≈ 2.259
 
*[[http://en.wikipedia.org/wiki/Cauchy's_equation Cauchy Parameters]] (350-2000nm):
 
*[[http://en.wikipedia.org/wiki/Cauchy's_equation Cauchy Parameters]] (350-2000nm):
−
** A = 2.435
 +
**A = 2.435
−
** B = -4.9045e-4
 +
**B = -4.9045e-4
−
** C = 0.01309
 +
**C = 0.01309
 
*Absorbing < ~350nm
  
*Absorbing < ~350nm
   
−
== Al2O3 deposition (IBD) ==
 +
==Al2O3 deposition (IBD)==
−
* Al2O3 standard recipe: 1_Al2O3_dep
  
   
  +
*Al2O3 standard recipe: 1_Al2O3_dep
−
* [https://docs.google.com/spreadsheets/d/1Qwxa7rtq2kGeFUQxnjGFgtdCJP4uIX_bdUcCWFvO72g/edit#gid= Al2O3 Data 2018]
  
  +
−
* [https://docs.google.com/spreadsheets/d/1rjwDQ0WJOIL7XWx2KWQ4fEPjNkr6GEmiXGmQXZnWFOI/edit#gid= Al2O3 Thickness uniformity 2018]
  
  +
*[https://docs.google.com/spreadsheets/d/1Qwxa7rtq2kGeFUQxnjGFgtdCJP4uIX_bdUcCWFvO72g/edit#gid= Al2O3 Data 2018]
  +
*[https://docs.google.com/spreadsheets/d/1rjwDQ0WJOIL7XWx2KWQ4fEPjNkr6GEmiXGmQXZnWFOI/edit#gid= Al2O3 Thickness uniformity 2018]
   
 
*Deposition Rate: ≈ 2.05nm/min (users must calibrate this prior to critical deps)
  
*Deposition Rate: ≈ 2.05nm/min (users must calibrate this prior to critical deps)
Line 390: Line 458:
 
*Refractive Index: ≈ 1.656
  
*Refractive Index: ≈ 1.656
 
*[[http://en.wikipedia.org/wiki/Cauchy's_equation Cauchy Parameters]] (350-2000nm):( working on)
 
*[[http://en.wikipedia.org/wiki/Cauchy's_equation Cauchy Parameters]] (350-2000nm):( working on)
−
** A =
+
**A =
−
** B =
+
**B =
−
** C =
+
**C =
 
*Absorbing < ~350nm
  
*Absorbing < ~350nm
   
   
−
=[[Sputter 2 (SFI Endeavor)]]=
  
−
'''This Tool has been Removed from the Cleanroom! These recipes are displayed here for historical/reference purposes only.'''
  
   
  +
= [[Sputter 2 (SFI Endeavor)|<big><u>Sputter 2 (SFI Endeavor)</u></big>]] =
−
== Al Deposition (Sputter 2) ==
  
  +
'''This Tool has been Disabled, and is not available for use any more! These recipes are displayed here for historical/reference purposes only.'''
−
*[[media:20-Al-Sputtering-Film-Sputter-2.pdf|Al Deposition Recipe]]
  
  +
−
== AlN<sub>x</sub> Deposition (Sputter 2) ==
  
  +
==Al Deposition (Sputter 2)==
−
*[[media:Sputter-2-AlN-Endeavor-rev1.pdf|AlN<sub>x</sub> Deposition Recipe]]
  
  +
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/0/05/20-Al-Sputtering-Film-Sputter-2.pdf Al Deposition Recipe]
  +
  +
==AlN<sub>x</sub> Deposition (Sputter 2)==
  +
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/8/8c/Sputter-2-AlN-Endeavor-rev1.pdf AlN<sub>x</sub> Deposition Recipe]
  +
  +
==Au Deposition (Sputter 2)==
  +
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/8/8a/21-Au-Sputter-film-recipes-Sputter-2.pdf Au Deposition Recipe]
  +
  +
==TiO<sub>2</sub> Deposition (Sputter 2)==
   
  +
*[//wiki.nanotech.ucsb.edu/wiki/images/c/c4/22-TiO2-Film-Sputter-2.pdf TiO2<sub>2</sub> Deposition Recipe]
−
== Au Deposition (Sputter 2) ==
  
−
*[[media:21-Au-Sputter-film-recipes-Sputter-2.pdf|Au Deposition Recipe]]
  
−
== TiO<sub>2</sub> Deposition (Sputter 2) ==
  
−
*[[media:22-TiO2-Film-Sputter-2.pdf|TiO2<sub>2</sub> Deposition Recipe]]
  

Revision as of 09:58, 23 April 2020

Back to Vacuum Deposition Recipes. R

Sputter 3 (AJA ATC 2000-F)

The recipes below are given as starting points from data obtained in the nanofab. For critical depositions, calibrations are recommended. Please see the SignupMonkey Page for a list of currently installed targets.

Material P(mT) Pow(W) Sub(W) T(C) Ar N2 O2 Height-Tilt Rate(nm/min) Stress(MPa) Rs(uOhm-cm) n@633nm k@633nm Target Consumed Lower Limit Data Below Comment
Au - - - - - - - - - - - - - Set: 200 W

Read: 400 VDC

no
Al2O3 3 200 (RF2) off 20 30 1.5 1.52"-4mm 5.32 1.6478 0 no Demis D. John
Co 10(5) 200 0 20 25 0 0 25-9 2.3 - - - - yes Alex K
Cr 5 200 0 20 25 0 0 44-4 6.84 - - - - no Brian
Cu 1.5 50(395v) 0 20 25 0 0 25-9 4.15 - - - - no Ning
Cu 5 150(~490v) 0 20 15 0 0 0.82"-9 8 - - - - yes Ning
Fe 10(5) 200 0 20 25 0 0 25-9 1.25 - - - - No Alex K
Mo 3 200 0 20 25 0 0 44-4 13.15 - - - - yes Ning
Ni 5 150 0 20 25 0 0 44-4 5.23 - - - - yes Ning
Ni 5 150 0 20 25 0 0 25-9 1.82 - - - - yes Ning
Ni 5 75 0 20 25 0 0 44-4 2.50 - - - - yes Ning
Ni 3 200 0 20 25 0 0 44-4 9.4 - - - - yes Ning
Ni 1.5 50(399v) 0 20 25 0 0 25-9 0.96 - - - - no Ning
Pt 3 50 0 20 25 0 0 0.82"-9 2.9 - - - - no Ning
Si 8 250 0 25 25 0 0 15-3 1.4 - - - - no Gerhard - ramp 2W/s - 3% Unif 4" wafer
SiN 3 200 10 20 25 3 0 25-9 1.56 - - 1.992 - yes Brian
SiN 3 250 10 20 25 2.5 0 25-9 2.1 - - 2.06 - yes Brian
SiO2 3 200 10 20 25 0 3 25-9 3.68 - - 1.447 - yes Brian
SiO2 3 200 10 20 25 0 5 45-3 2.60 - - 1.471 - yes Brian
SiO2 3 250 10 20 25 0 2.5 25-9 4.3 - - 1.485 - yes Brian
Ta 5 150 0 20 25 0 0 44-4 9.47 - - - - yes Ning
Ta 5 75 0 20 25 0 0 44-4 5.03 - - - - yes Ning
Ti 3 100 0 20 25 0 0 25-9 1.34 - - - - yes Ning
SampleClean-NativeSiO2 10 0 18 20 25 0 0 44-4 - - - - - yes 150Volts 5 min

Height Conversion for Older Recipes

Old recipes using the manual Height setting in millimeters can be converted to the new programmatic settings in inches as follows:

Old (mm) New (inches) Typical Gun Tilt (mm)
15
25 0.82 9
44 1.52 4

Interpolation plot can be found here.

Fe and Co Deposition (Sputter 3)

Cu Deposition (Sputter 3)

Mo Deposition (Sputter 3)

Ni and Ta Deposition (Sputter 3)

SiO2 Deposition (Sputter 3)

SiN Deposition (Sputter 3)

Ti Deposition (Sputter 3)

Sputter 4 (AJA ATC 2200-V)

The recipes below are given as starting points from data obtained in the nanofab. For critical depositions, calibrations are recommended. Please see the SignupMonkey page for a list of currently installed targets.

Material P(mT) Power Source Pow(W) Sub(W) T(C) Ar N2 O2 Height-Tilt Rate(nm/min) Stress(MPa) Rs(uOhm-cm) n@633nm k@633nm Data Below Comment
Al 5 200 0 20 45 0 0 H2.75-T5 4.4 - - - - Yes Ning Cao
Al2O3 3 RF4-Sw1 200 0 20 30 0 1.5 H2.75-T5 5.1 1.64202 0 partial Demis D. John
Au 5 200 0 20 45 0 0 H1-T10 17.7 - - - - Yes Ning Cao
Au 10 300 0 20 45 0 0 H2.75-T5 45.4 - - - - Yes Ning Cao
Cu 5 150 0 20 30 0 0 H0.82-T9 6.7 No (SEM available) Ning Cao
Nb 4 250 0 20 30 0 0 H2.00-T7 7.5 - - - - No
Pt 5 200 0 20 45 0 0 H2.75-T5 7.4 - - - - Yes Ning Cao
Pt 3 50(439V) 0 20 45 0 0 H2.75-T5 3.9 - - - - Yes Ning Cao
Ti 10 200 0 20 45 0 0 H2.75-T5 2.3 - - - - Yes Ning Cao
TiN 3 150 110V 20 48.25 1.75 0 H2.5-T5 2 - 60 - - No
TiO2 3 250(RF:450V) 0 20 45 0 3 H2.75-T5 4.3 - - - Yes Ning Cao
TiW 4.5 200 0 20 45 0 0 H1-T10 4.7 - - - - Yes Ning Cao
TiW 4.5 300 0 75 45 0 0 H2.75-T5 9.5 -150 to 150 60 - - Yes 10%Ti by Wt
W 3 300 0 50 45 0 0 H2.75-T5 11.5 -150 to 150 11 - - Yes Jeremy Watcher

W-TiW Deposition (Sputter 4)

Ti-Au Deposition (Sputter 4)

Pt Deposition (Sputter 4)

TiW Deposition (Sputter 4)

TiO2 Deposition (Sputter 4)

Au Deposition (Sputter 4)

Al Deposition (Sputter 4)

Al2O3 Deposition (Sputter 4)

  • Rate: 5.134 nm/min
  • Cauchy Refractive Index Params (fit from λ=190-1700nm, indicating transparency over this range)
    • A = 1.626
    • B = 5.980E-3
    • C = 1.622E-4

Sputter 5 (AJA ATC 2200-V)

The recipes below are given as starting points from data obtained in the nanofab. For critical depositions, calibrations are recommended.

Please see the SignupMonkey page for a list of currently installed targets.

Material P(mT) Power Source Pow(W) Sub(V) T(C) Ar N2 O2 Height-Tilt Rate(nm/min) Stress(MPa) Rs(uOhm-cm) Rq(nm) n@633nm k@633nm LPDb/LPDa* Data Below Comment
Al 5 250 0 20 45 0 0 H1-T10 2.5 22 No (SEM available) Ning
Al2O3 1.5 DC5-SW1 150 - - 45 - 5 H2.75-T5 5.3 ? ? ? 1.641 - ? No Demis 2018-04-13
SiO2 3 250 120 20 45 0 2 H1.0-T10 2.32 - - 1.49 - 153/6384 No Biljana
SiO2 3 250 120 20 45 0 4.5 H1.0-T10 2.29 -515 - 0.210 1.49 138/4445 No ( AFM available) Biljana
SiO2 3 250 120 20 45 0 6 H1.0-T10 2.32 - - 1.49 - 27/1515 Yes Biljana

*LPD: light particle detection:

  • LPDb: light particle detection before deposition
  • LPDa: light particle detection after deposition

SiO2 Deposition (Sputter 5)

Ion Beam Deposition (Veeco NEXUS)

SiO2 deposition (IBD)

SiO2 1hr deposition properties:
  • Dep.rate: ≈ 5.2 nm/min (users must calibrate this prior to critical deps)
  • HF e.r.~350 nm/min
  • Stress ≈ -390MPa (compressive)
  • Refractive Index: ≈ 1.494
  • [Cauchy Parameters] (350-2000nm):
    • A = 1.480
    • B = 0.00498
    • C = -3.2606e-5

Si3N4 deposition (IBD)

  • Deposition Rate: ≈ 4.10 nm/min (users must calibrate this prior to critical deps)
  • HF e.r.~11nm/min
  • Stress ≈ -1590MPa (compressive)
  • Refractive Index: ≈ 1.969
  • [Cauchy Parameters] (350-2000nm):
    • A = 2.000
    • B = 0.01974
    • C = 1.2478e-4

SiOxNy deposition (IBD)

These are some old (2010), initial characterizations only. A recipe improvement would be to increase the Assist O2+N2 = 60sccm total, increasing repeatability. Contact Demis for more info.

plot showing varying refractive index between Si3N4 and SiO2
IBD SiOxNy: Refractive Index vs. O2/N2 Flow.
Rate varies monotonically from 53-5 Å/min.
Dep. Rate of IBD SiOxNy vs. Assist O2 flow.

Ta2O5 deposition (IBD)


  • Ta2O5 1hr depositions:
  • Deposition Rate: ≈ 7.8 nm/min (users must calibrate this prior to critical deps)
  • HF e.r.~2 nm/min
  • Stress ≈ -232MPa (compressive)
  • Refractive Index: ≈ 2.172
  • [Cauchy Parameters] (350-2000nm):
    • A = 2.1123
    • B = 0.018901
    • C = -0.016222

TiO2 deposition (IBD)

  • Deposition Rate: ≈ 1.29 nm/min (users must calibrate this prior to critical deps)
  • HF etch rate ~5.34nm/min
  • Stress ≈ -445MPa (compressive)
  • Refractive Index: ≈ 2.259
  • [Cauchy Parameters] (350-2000nm):
    • A = 2.435
    • B = -4.9045e-4
    • C = 0.01309
  • Absorbing < ~350nm

Al2O3 deposition (IBD)

  • Al2O3 standard recipe: 1_Al2O3_dep
  • Deposition Rate: ≈ 2.05nm/min (users must calibrate this prior to critical deps)
  • HF etch rate ~167nm/min
  • Stress ≈ -332MPa (compressive)
  • Refractive Index: ≈ 1.656
  • [Cauchy Parameters] (350-2000nm):( working on)
    • A =
    • B =
    • C =
  • Absorbing < ~350nm


Sputter 2 (SFI Endeavor)

This Tool has been Disabled, and is not available for use any more! These recipes are displayed here for historical/reference purposes only.

Al Deposition (Sputter 2)

AlNx Deposition (Sputter 2)

Au Deposition (Sputter 2)

TiO2 Deposition (Sputter 2)

Retrieved from "https://wiki.nanofab.ucsb.edu/w/index.php?title=Sputtering_Recipes&oldid=158107"