PECVD 1 (PlasmaTherm 790)

SiN deposition (PECVD #1)

File:PECVD1-SiN-Recipe.pdf

SiO2 deposition (PECVD #1)

  1. Clean (30CLN_SN)
    1. Initial t=10", p=2x10-2, T=250C
    2. N2 Purge t=30", p=300mT
    3. evacuate, base pressure=2x10-2, t=10"
    4. loop
    5. gas stabilization, t=30"
    6. etch chamber, t=30'
    7. evacuate, t=10"
    8. N2 purge
    9. evacuate
    10. loop
    11. SiO2 gas stabilization
    12. SiO2 deposition( 200A coat)
    13. evacuate
    14. N2 purge, t=30"
    15. end
  2. SiO2 deposition (SiO2_10) 440.5 A/min
    1. Initial t=10"
    2. N2 purge t=30"
    3. evacuate, t=10"
    4. loop
    5. SiO2 gas stabilization, t=30"
    6. SiO2 deposition t=8'11.2"
    7. evacuate, t=10"
    8. N2 purge t=30"
    9. evacuate t=10"
    10. loop

PECVD 2 (Advanced Vacuum)

SiN deposition (PECVD #2)

  1. Standard clean
    1. Pump down: stabilization time t=15", step time(m)=0', step time(s)=30"
    2. Pre-purge: purge=1, stabilization time=15, step time(m)=1, step time(sec)=0
    3. High Pressure: process pressure=600, RF point=300, stabilization time=35, step time(m)=30, step time(s)=0, CF4/O2(5)=500
    4. Low pressure: process pressure=300, RF setpoint=300, stabilization time=15, step time(m)=30, step time(s)=0, CF4/O2(5)=500
  2. Nitride 2 (HF, n=2.0, 93nm/min)
    1. process pressure=800, RF setpoint=30, stabilization time=15, step time(m)=10, step time(s)=0, 2%SiH4%He(1)=1040, N2(3)=980, NH3(2)=17

SiO2 deposition (PECVD #2)

  1. Standard clean
    1. Pump down: stabilization time t=15", step time(m)=0', step time(s)=30"
    2. Pre-purge: purge=1, stabilization time=15, step time(m)=1, step time(sec)=0
    3. High Pressure: process pressure=600, RF point=300, stabilization time=35, step time(m)=30, step time(s)=0, CF4/O2(5)=500
    4. Low pressure: process pressure=300, RF setpoint=300, stabilization time=15, step time(m)=30, step time(s)=0, CF4/O2(5)=500
  2. Oxide (HF, n=1.46, 25nm/min)
    1. process pressure=800, RF setpoint=30, stabilization time=15, step time(m)=10, step time(s)=0, 2%SiH4%He(1)=600, N2O(4)=1420

ICP-PECVD (Unaxis VLR)