Difference between revisions of "OLD - PECVD2 Recipes"
Jump to navigation
Jump to search
| Line 5: | Line 5: | ||
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dERkYm85bGtYQVpjVk5GTGJuMkg2anc&usp=drive_web#gid=sharing Nitride2 Thickness uniformity 2014] |
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dERkYm85bGtYQVpjVk5GTGJuMkg2anc&usp=drive_web#gid=sharing Nitride2 Thickness uniformity 2014] |
||
| − | *Deposition Rate: ≈ 8. |
+ | *Deposition Rate: ≈ 8.17 nm/min (users must calibrate this prior to critical deps) |
| − | *Refractive Index: ≈ 1. |
+ | *Refractive Index: ≈ 1.957 |
| − | *Stress ≈ |
+ | *Stress ≈ 499MPa |
| − | *HF etch rate:~ |
+ | *HF etch rate:~49nm/min |
== SiO<sub>2</sub> deposition (PECVD #2) == |
== SiO<sub>2</sub> deposition (PECVD #2) == |
||
Revision as of 15:57, 1 August 2014
PECVD 2 (Advanced Vacuum)
SiN deposition (PECVD #2)
- Deposition Rate: ≈ 8.17 nm/min (users must calibrate this prior to critical deps)
- Refractive Index: ≈ 1.957
- Stress ≈ 499MPa
- HF etch rate:~49nm/min
SiO2 deposition (PECVD #2)
- Deposition Rate: ≈ 28.36 nm/min (users must calibrate this prior to critical deps)
- Refractive Index: ≈ 1.473
- Stress ≈ -256MPa
- HF etch rate~582nm/min
LS SiN deposition (PECVD #2)
- Deposition Rate: ≈ 8.17 nm/min (users must calibrate this prior to critical deps)
- Refractive Index: ≈ 1.935
- Stress ≈ -0.04MPa
- HF etch rate~47nm/min