E-Beam 2 (Custom)

E-Beam 2 (Custom) Tool Type Vacuum Deposition Location Bay 3 Supervisor Tony Bosch Supervisor Phone (805) 893-3486 Supervisor E-Mail bosch@ece.ucsb.edu Description Electron-Beam Evaporation System Manufacturer Temescal Vacuum Deposition Recipes Sign up for this tool

About

This electron-beam evaporation system is used for the controlled deposition of thin dielectric films. The films are evaporated from a wide variety of solid sources. The most common dielectrics deposited are: SiO₂, SiO, TiO₂, Ta₂O₅, SrF₂. Other materials may be evaporated upon request. Oxygen gas can be bled into the system during deposition to try to maintain the stoichiometry during deposition. Fixturing for heating the substrate can also be used. A crystal thickness monitor is used to control the deposition thickness. The dielectrics deposited by this system are typically used for optical coatings (anti-reflective and highly reflective multiple layer stacks), electrical insulators, and reactive ion etching masks. Samples up to ~ 3” x 3” can be placed into this system for evaporation. Typical deposition rates are several Angstroms/second.

Detailed Specifications

• Temescal 10kV power supply
• Temescal 4-pocket series 260 e-beam source
• Electron beam controller with sweep rate and amplitude control
• Cryo-pumped system with ~ 1e-7 ultimate base pressure
• Automatic vacuum sequencing
• Crystal thickness monitoring
• Sample size: up to 3” x 3” pieces
• Oxygen bleed for maintaining oxide stoichiometry

Materials Table

Materials Table
Material	Density, g/cm3	Z Ratio	Tooling factor, %	Comments
Al2O3	3.97	0.336	140	Check this
GeO2	5.35	0.516		Check this
ITO	6.43-7.16	0.841		Check this
MgO2	3.58	0.411	157.6	Check this
Si	2.32	0.712	150.0	Check this
SiO2	2.70	1.070	157.6	Check this
SiOx	2.13	0.87	130.0	Check this
SrF2	4.28	0.727	140.0	Check this
Ta2O5	8.2	0.30	157.6	Check this
TiO2	4.26	0.400	139.0	Check this